- 密度 [g/cm3]: 1.14
- 弯曲强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 0.466
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | DIN 53714: 23°C, 50% Relative Humidity |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 527 |
| Elongation at Break | 370 % | 370 % | ISO 527 |
| Modulus of Elasticity | 0.431 GPa | 62.5 ksi | ISO 527 |
| Flexural Modulus | 0.466 GPa | 67.6 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180, No break |
| 30.0 kJ/m² @Temperature -40.0 °C | 14.3 ft-lb/in² @Temperature -40.0 °F | Ductile break; ISO 180 | |
| Charpy Impact, Notched | NB | NB | No break |
| NB | NB | Low Temp | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.00e+9 ohm-cm | 4.00e+9 ohm-cm | DIN 53482 |
| Surface Resistance | 3.00e+8 ohm | 3.00e+8 ohm | DIN 53482 |
| Dielectric Constant | 4.6 @Frequency 1e+6 Hz | 4.6 @Frequency 1e+6 Hz | DIN 53483 |
| 14.9 @Frequency 50 Hz | 14.9 @Frequency 50 Hz | DIN 53483 | |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | DIN 53481 |
| Dissipation Factor | 0.10 @Frequency 1e+6 Hz | 0.10 @Frequency 1e+6 Hz | DIN 53483 |
| Comparative Tracking Index | 600 V | 600 V | DIN IEC 112 / VDE 030 t1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 213 °C | 415 °F | DSC |