DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6

DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 物性表: DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6物性表及特性介绍,DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6注塑参数详情,如需DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 吸水率 [%]: 1.8
  • 缺口冲击强度: 4.0
  • 弯曲模量 [MPa]: 5.90
  • 热变形温度 [℃]: 196.0
 
Physical PropertiesMetricEnglishComments
Density 1.45 g/cc0.0524 lb/in³DAM; ISO 1183
Filler Content 40 %40 %DAM
Water Absorption  1.8 %
@Temperature 23.0 °C		1.8 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 5.4 %
@Temperature 23.0 °C		5.4 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  59.0 MPa
@Temperature 23.0 °C		8560 psi
@Temperature 73.4 °F		50%RH; ISO 527
 87.0 MPa
@Temperature 23.0 °C		12600 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  4.89 MPa
@Strain 0.200 %,
Temperature 60.0 °C		709 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.15 MPa
@Strain 1.23 %,
Temperature 150 °C		747 psi
@Strain 1.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.36 MPa
@Strain 1.23 %,
Temperature 120 °C		922 psi
@Strain 1.23 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.55 MPa
@Strain 0.600 %,
Temperature 90.0 °C		1100 psi
@Strain 0.600 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 7.66 MPa
@Strain 1.22 %,
Temperature 90.0 °C		1110 psi
@Strain 1.22 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 8.07 MPa
@Strain 0.830 %,
Temperature 120 °C		1170 psi
@Strain 0.830 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.34 MPa
@Strain 2.43 %,
Temperature 150 °C		1210 psi
@Strain 2.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.62 MPa
@Strain 1.25 %,
Temperature 150 °C		1250 psi
@Strain 1.25 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.37 MPa
@Strain 2.42 %,
Temperature 120 °C		1504 psi
@Strain 2.42 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.54 MPa
@Strain 3.63 %,
Temperature 150 °C		1529 psi
@Strain 3.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.86 MPa
@Strain 1.23 %,
Temperature 60.0 °C		1575 psi
@Strain 1.23 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.15 MPa
@Strain 4.83 %,
Temperature 150 °C		1762 psi
@Strain 4.83 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.35 MPa
@Strain 2.42 %,
Temperature 90.0 °C		1791 psi
@Strain 2.42 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 12.49 MPa
@Strain 1.23 %,
Temperature 40.0 °C		1812 psi
@Strain 1.23 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 13.19 MPa
@Strain 3.62 %,
Temperature 120 °C		1913 psi
@Strain 3.62 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.32 MPa
@Strain 6.03 %,
Temperature 150 °C		1932 psi
@Strain 6.03 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.86 MPa
@Strain 0.250 %,
Temperature 40.0 °C		2010 psi
@Strain 0.250 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 14.29 MPa
@Strain 7.23 %,
Temperature 150 °C		2073 psi
@Strain 7.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.07 MPa
@Strain 8.43 %,
Temperature 150 °C		2186 psi
@Strain 8.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.3 MPa
@Strain 4.82 %,
Temperature 120 °C		2220 psi
@Strain 4.82 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 3.61 %,
Temperature 90.0 °C		2280 psi
@Strain 3.61 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 9.63 %,
Temperature 150 °C		2281 psi
@Strain 9.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.52 MPa
@Strain 3.60 %,
Temperature 150 °C		2396 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.9 MPa
@Strain 6.02 %,
Temperature 120 °C		2450 psi
@Strain 6.02 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.08 MPa
@Strain 2.43 %,
Temperature 60.0 °C		2477 psi
@Strain 2.43 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.24 MPa
@Strain 1.23 %,
Temperature 23.0 °C		2500 psi
@Strain 1.23 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.22 MPa
@Strain 7.21 %,
Temperature 120 °C		2643 psi
@Strain 7.21 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 2.69 %,
Temperature 120 °C		2650 psi
@Strain 2.69 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.34 MPa
@Strain 4.81 %,
Temperature 90.0 °C		2660 psi
@Strain 4.81 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 19.28 MPa
@Strain 8.41 %,
Temperature 120 °C		2796 psi
@Strain 8.41 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.6 MPa
@Strain 2.44 %,
Temperature 40.0 °C		2840 psi
@Strain 2.44 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 19.84 MPa
@Strain 1.05 %,
Temperature 60.0 °C		2878 psi
@Strain 1.05 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.11 MPa
@Strain 2.26 %,
Temperature 90.0 °C		2917 psi
@Strain 2.26 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 20.19 MPa
@Strain 9.61 %,
Temperature 120 °C		2928 psi
@Strain 9.61 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.36 MPa
@Strain 6.00 %,
Temperature 90.0 °C		2953 psi
@Strain 6.00 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.62 MPa
@Strain 6.14 %,
Temperature 150 °C		2991 psi
@Strain 6.14 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.94 MPa
@Strain 10.81 %,
Temperature 120 °C		3037 psi
@Strain 10.81 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.41 MPa
@Strain 3.64 %,
Temperature 60.0 °C		3105 psi
@Strain 3.64 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 12.0 %,
Temperature 120 °C		3130 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.08 MPa
@Strain 7.26 %,
Temperature 90.0 °C		3202 psi
@Strain 7.26 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.1 MPa
@Strain 8.78 %,
Temperature 150 °C		3350 psi
@Strain 8.78 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.1 MPa
@Strain 0.380 %,
Temperature 0.000 °C		3350 psi
@Strain 0.380 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.41 MPa
@Strain 8.45 %,
Temperature 90.0 °C		3395 psi
@Strain 8.45 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.0 MPa
@Strain 4.70 %,
Temperature 120 °C		3480 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.51 MPa
@Strain 9.65 %,
Temperature 90.0 °C		3555 psi
@Strain 9.65 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.53 MPa
@Strain 3.64 %,
Temperature 40.0 °C		3558 psi
@Strain 3.64 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 24.67 MPa
@Strain 4.84 %,
Temperature 60.0 °C		3578 psi
@Strain 4.84 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.8 MPa
@Strain 11.54 %,
Temperature 150 °C		3600 psi
@Strain 11.54 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.65 MPa
@Strain 2.43 %,
Temperature 23.0 °C		3720 psi
@Strain 2.43 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.05 MPa
@Strain 14.36 %,
Temperature 150 °C		3778 psi
@Strain 14.36 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.06 MPa
@Strain 17.23 %,
Temperature 150 °C		3925 psi
@Strain 17.23 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.07 MPa
@Strain 6.04 %,
Temperature 60.0 °C		3926 psi
@Strain 6.04 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.53 MPa
@Strain 6.90 %,
Temperature 120 °C		3993 psi
@Strain 6.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.57 MPa
@Strain 4.08 %,
Temperature 90.0 °C		3999 psi
@Strain 4.08 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 27.85 MPa
@Strain 0.460 %,
Temperature -40.0 °C		4039 psi
@Strain 0.460 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 27.87 MPa
@Strain 20.15 %,
Temperature 150 °C		4042 psi
@Strain 20.15 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.92 MPa
@Strain 0.470 %,
Temperature 23.0 °C		4049 psi
@Strain 0.470 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.29 MPa
@Strain 4.85 %,
Temperature 40.0 °C		4103 psi
@Strain 4.85 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 28.53 MPa
@Strain 23.16 %,
Temperature 150 °C		4138 psi
@Strain 23.16 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.97 MPa
@Strain 7.24 %,
Temperature 60.0 °C		4202 psi
@Strain 7.24 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.08 MPa
@Strain 26.18 %,
Temperature 150 °C		4218 psi
@Strain 26.18 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.57 MPa
@Strain 29.22 %,
Temperature 150 °C		4289 psi
@Strain 29.22 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.86 MPa
@Strain 9.16 %,
Temperature 120 °C		4331 psi
@Strain 9.16 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.35 MPa
@Strain 2.27 %,
Temperature 60.0 °C		4402 psi
@Strain 2.27 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.42 MPa
@Strain 8.44 %,
Temperature 60.0 °C		4412 psi
@Strain 8.44 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.94 MPa
@Strain 3.63 %,
Temperature 23.0 °C		4487 psi
@Strain 3.63 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.16 MPa
@Strain 6.05 %,
Temperature 40.0 °C		4519 psi
@Strain 6.05 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 31.5 MPa
@Strain 11.48 %,
Temperature 120 °C		4570 psi
@Strain 11.48 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.59 MPa
@Strain 9.65 %,
Temperature 60.0 °C		4582 psi
@Strain 9.65 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.34 MPa
@Strain 6.02 %,
Temperature 90.0 °C		4691 psi
@Strain 6.02 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 32.75 MPa
@Strain 13.84 %,
Temperature 120 °C		4750 psi
@Strain 13.84 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.06 MPa
@Strain 0.460 %,
Temperature -20.0 °C		4795 psi
@Strain 0.460 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 33.46 MPa
@Strain 7.26 %,
Temperature 40.0 °C		4853 psi
@Strain 7.26 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 33.72 MPa
@Strain 16.3 %,
Temperature 120 °C		4891 psi
@Strain 16.3 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.54 MPa
@Strain 18.84 %,
Temperature 120 °C		5010 psi
@Strain 18.84 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.96 MPa
@Strain 4.83 %,
Temperature 23.0 °C		5071 psi
@Strain 4.83 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.15 MPa
@Strain 8.40 %,
Temperature 40.0 °C		5098 psi
@Strain 8.40 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.2 MPa
@Strain 21.39 %,
Temperature 120 °C		5110 psi
@Strain 21.39 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.5 MPa
@Strain 8.06 %,
Temperature 90.0 °C		5150 psi
@Strain 8.06 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 35.77 MPa
@Strain 23.98 %,
Temperature 120 °C		5188 psi
@Strain 23.98 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.59 MPa
@Strain 9.61 %,
Temperature 40.0 °C		5307 psi
@Strain 9.61 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.88 MPa
@Strain 3.56 %,
Temperature 60.0 °C		5349 psi
@Strain 3.56 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.44 MPa
@Strain 1.12 %,
Temperature 0.000 °C		5430 psi
@Strain 1.12 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.68 MPa
@Strain 10.21 %,
Temperature 90.0 °C		5465 psi
@Strain 10.21 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 37.71 MPa
@Strain 10.81 %,
Temperature 40.0 °C		5469 psi
@Strain 10.81 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 38.09 MPa
@Strain 6.03 %,
Temperature 23.0 °C		5524 psi
@Strain 6.03 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.64 MPa
@Strain 12.02 %,
Temperature 40.0 °C		5604 psi
@Strain 12.02 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 39.29 MPa
@Strain 12.38 %,
Temperature 90.0 °C		5699 psi
@Strain 12.38 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 39.47 MPa
@Strain 0.740 %,
Temperature -20.0 °C		5725 psi
@Strain 0.740 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 40.16 MPa
@Strain 0.640 %,
Temperature 0.000 °C		5825 psi
@Strain 0.640 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.45 MPa
@Strain 0.660 %,
Temperature -40.0 °C		5867 psi
@Strain 0.660 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 40.53 MPa
@Strain 14.56 %,
Temperature 90.0 °C		5878 psi
@Strain 14.56 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 40.61 MPa
@Strain 7.23 %,
Temperature 23.0 °C		5890 psi
@Strain 7.23 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.94 MPa
@Strain 0.800 %,
Temperature 40.0 °C		5938 psi
@Strain 0.800 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.47 MPa
@Strain 4.87 %,
Temperature 60.0 °C		6015 psi
@Strain 4.87 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.54 MPa
@Strain 16.86 %,
Temperature 90.0 °C		6025 psi
@Strain 16.86 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 42.34 MPa
@Strain 19.17 %,
Temperature 90.0 °C		6141 psi
@Strain 19.17 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 42.58 MPa
@Strain 8.43 %,
Temperature 23.0 °C		6176 psi
@Strain 8.43 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.08 MPa
@Strain 21.52 %,
Temperature 90.0 °C		6248 psi
@Strain 21.52 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 43.52 MPa
@Strain 0.740 %,
Temperature 23.0 °C		6312 psi
@Strain 0.740 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.63 MPa
@Strain 23.86 %,
Temperature 90.0 °C		6328 psi
@Strain 23.86 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 44.15 MPa
@Strain 9.62 %,
Temperature 23.0 °C		6403 psi
@Strain 9.62 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.89 MPa
@Strain 6.27 %,
Temperature 60.0 °C		6511 psi
@Strain 6.27 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.36 MPa
@Strain 10.82 %,
Temperature 23.0 °C		6579 psi
@Strain 10.82 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.36 MPa
@Strain 12.02 %,
Temperature 23.0 °C		6724 psi
@Strain 12.02 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.11 MPa
@Strain 13.22 %,
Temperature 23.0 °C		6833 psi
@Strain 13.22 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.37 MPa
@Strain 7.66 %,
Temperature 60.0 °C		6870 psi
@Strain 7.66 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.7 MPa
@Strain 14.42 %,
Temperature 23.0 °C		6920 psi
@Strain 14.42 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.17 MPa
@Strain 0.680 %,
Temperature -20.0 °C		6986 psi
@Strain 0.680 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 49.33 MPa
@Strain 9.07 %,
Temperature 60.0 °C		7155 psi
@Strain 9.07 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.84 MPa
@Strain 10.54 %,
Temperature 60.0 °C		7374 psi
@Strain 10.54 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.03 MPa
@Strain 11.97 %,
Temperature 60.0 °C		7546 psi
@Strain 11.97 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.45 MPa
@Strain 2.16 %,
Temperature 0.000 °C		7607 psi
@Strain 2.16 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.82 MPa
@Strain 0.870 %,
Temperature -40.0 °C		7661 psi
@Strain 0.870 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 53.02 MPa
@Strain 13.49 %,
Temperature 60.0 °C		7690 psi
@Strain 13.49 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.88 MPa
@Strain 14.98 %,
Temperature 60.0 °C		7815 psi
@Strain 14.98 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.58 MPa
@Strain 16.53 %,
Temperature 60.0 °C		7916 psi
@Strain 16.53 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.68 MPa
@Strain 0.900 %,
Temperature 0.000 °C		8076 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 55.89 MPa
@Strain 1.32 %,
Temperature 40.0 °C		8106 psi
@Strain 1.32 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 56.77 MPa
@Strain 0.990 %,
Temperature 23.0 °C		8234 psi
@Strain 0.990 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.2 MPa
@Strain 3.25 %,
Temperature 0.000 °C		8440 psi
@Strain 3.25 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.91 MPa
@Strain 0.880 %,
Temperature -20.0 °C		8834 psi
@Strain 0.880 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 60.98 MPa
@Strain 4.29 %,
Temperature 0.000 °C		8844 psi
@Strain 4.29 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.04 MPa
@Strain 5.38 %,
Temperature 0.000 °C		9143 psi
@Strain 5.38 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.99 MPa
@Strain 2.00 %,
Temperature 40.0 °C		9281 psi
@Strain 2.00 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 64.75 MPa
@Strain 6.48 %,
Temperature 0.000 °C		9391 psi
@Strain 6.48 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.12 MPa
@Strain 1.07 %,
Temperature -40.0 °C		9445 psi
@Strain 1.07 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 66.1 MPa
@Strain 7.51 %,
Temperature 0.000 °C		9590 psi
@Strain 7.51 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.28 MPa
@Strain 2.93 %,
Temperature 40.0 °C		9613 psi
@Strain 2.93 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 66.48 MPa
@Strain 1.10 %,
Temperature 0.000 °C		9642 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.73 MPa
@Strain 1.22 %,
Temperature 23.0 °C		9678 psi
@Strain 1.22 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.89 MPa
@Strain 3.97 %,
Temperature 40.0 °C		9702 psi
@Strain 3.97 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 67.0 MPa
@Strain 1.49 %,
Temperature -20.0 °C		9720 psi
@Strain 1.49 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 67.28 MPa
@Strain 8.61 %,
Temperature 0.000 °C		9758 psi
@Strain 8.61 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.61 MPa
@Strain 5.02 %,
Temperature 40.0 °C		9806 psi
@Strain 5.02 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 68.29 MPa
@Strain 9.70 %,
Temperature 0.000 °C		9905 psi
@Strain 9.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.33 MPa
@Strain 6.04 %,
Temperature 40.0 °C		9910 psi
@Strain 6.04 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 69.0 MPa
@Strain 7.15 %,
Temperature 40.0 °C		10000 psi
@Strain 7.15 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 69.07 MPa
@Strain 10.74 %,
Temperature 0.000 °C		10020 psi
@Strain 10.74 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.64 MPa
@Strain 8.21 %,
Temperature 40.0 °C		10100 psi
@Strain 8.21 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 69.78 MPa
@Strain 11.83 %,
Temperature 0.000 °C		10120 psi
@Strain 11.83 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.17 MPa
@Strain 9.22 %,
Temperature 40.0 °C		10180 psi
@Strain 9.22 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 70.6 MPa
@Strain 10.35 %,
Temperature 40.0 °C		10200 psi
@Strain 10.35 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 71.57 MPa
@Strain 1.07 %,
Temperature -20.0 °C		10380 psi
@Strain 1.07 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 75.39 MPa
@Strain 1.26 %,
Temperature -40.0 °C		10930 psi
@Strain 1.26 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.62 MPa
@Strain 1.48 %,
Temperature 23.0 °C		10970 psi
@Strain 1.48 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.67 MPa
@Strain 1.31 %,
Temperature 0.000 °C		11120 psi
@Strain 1.31 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 79.7 MPa
@Strain 2.21 %,
Temperature -20.0 °C		11600 psi
@Strain 2.21 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 80.7 MPa
@Strain 1.23 %,
Temperature -20.0 °C		11700 psi
@Strain 1.23 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 83.36 MPa
@Strain 1.78 %,
Temperature 23.0 °C		12090 psi
@Strain 1.78 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 1.43 %,
Temperature -40.0 °C		12200 psi
@Strain 1.43 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 84.89 MPa
@Strain 2.97 %,
Temperature -20.0 °C		12310 psi
@Strain 2.97 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 85.98 MPa
@Strain 1.55 %,
Temperature 0.000 °C		12470 psi
@Strain 1.55 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.88 MPa
@Strain 3.69 %,
Temperature -20.0 °C		12600 psi
@Strain 3.69 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 87.95 MPa
@Strain 4.44 %,
Temperature -20.0 °C		12760 psi
@Strain 4.44 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 88.67 MPa
@Strain 1.40 %,
Temperature -20.0 °C		12860 psi
@Strain 1.40 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 88.69 MPa
@Strain 5.16 %,
Temperature -20.0 °C		12860 psi
@Strain 5.16 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 88.78 MPa
@Strain 2.13 %,
Temperature 23.0 °C		12880 psi
@Strain 2.13 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 91.6 MPa
@Strain 1.58 %,
Temperature -40.0 °C		13300 psi
@Strain 1.58 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.16 MPa
@Strain 2.56 %,
Temperature 23.0 °C		13370 psi
@Strain 2.56 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 93.31 MPa
@Strain 3.10 %,
Temperature 23.0 °C		13530 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 93.81 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13610 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.65 MPa
@Strain 1.60 %,
Temperature -20.0 °C		14020 psi
@Strain 1.60 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 99.0 MPa
@Strain 1.76 %,
Temperature -40.0 °C		14400 psi
@Strain 1.76 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.39 MPa
@Strain 2.10 %,
Temperature 0.000 °C		14560 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 103.83 MPa
@Strain 1.82 %,
Temperature -20.0 °C		15059 psi
@Strain 1.82 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 105.38 MPa
@Strain 2.46 %,
Temperature 0.000 °C		15284 psi
@Strain 2.46 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 105.77 MPa
@Strain 1.94 %,
Temperature -40.0 °C		15341 psi
@Strain 1.94 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.25 MPa
@Strain 2.89 %,
Temperature 0.000 °C		15700 psi
@Strain 2.89 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 109.43 MPa
@Strain 3.41 %,
Temperature 0.000 °C		15872 psi
@Strain 3.41 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 110.15 MPa
@Strain 2.08 %,
Temperature -20.0 °C		15976 psi
@Strain 2.08 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 112.15 MPa
@Strain 2.13 %,
Temperature -40.0 °C		16266 psi
@Strain 2.13 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.17 MPa
@Strain 2.37 %,
Temperature -20.0 °C		16704 psi
@Strain 2.37 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 117.66 MPa
@Strain 2.32 %,
Temperature -40.0 °C		17065 psi
@Strain 2.32 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.92 MPa
@Strain 2.70 %,
Temperature -20.0 °C		17248 psi
@Strain 2.70 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 121.44 MPa
@Strain 3.10 %,
Temperature -20.0 °C		17613 psi
@Strain 3.10 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 122.61 MPa
@Strain 2.54 %,
Temperature -40.0 °C		17783 psi
@Strain 2.54 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 122.75 MPa
@Strain 3.53 %,
Temperature -20.0 °C		17803 psi
@Strain 3.53 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 127.22 MPa
@Strain 2.79 %,
Temperature -40.0 °C		18452 psi
@Strain 2.79 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 130.93 MPa
@Strain 3.04 %,
Temperature -40.0 °C		18990 psi
@Strain 3.04 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 133.68 MPa
@Strain 3.33 %,
Temperature -40.0 °C		19389 psi
@Strain 3.33 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 135.73 MPa
@Strain 3.64 %,
Temperature -40.0 °C		19686 psi
@Strain 3.64 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137.46 MPa
@Strain 3.98 %,
Temperature -40.0 °C		19937 psi
@Strain 3.98 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 138.48 MPa
@Strain 4.29 %,
Temperature -40.0 °C		20085 psi
@Strain 4.29 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  10 %
@Temperature 23.0 °C		10 %
@Temperature 73.4 °F		DAM; ISO 527
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  2.20 GPa
@Temperature 23.0 °C		319 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 6.00 GPa
@Temperature 23.0 °C		870 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 5.90 GPa
@Temperature 23.0 °C		856 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  9.50 J/cm²
@Temperature -30.0 °C		45.2 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 9.50 J/cm²
@Temperature -30.0 °C		45.2 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 13.0 J/cm²
@Temperature 23.0 °C		61.9 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.500 J/cm²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.800 J/cm²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  75.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		41.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 75.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		41.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 196 °C385 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 110 °C230 °FDAM; ISO 75-1/-2
UL RTI, Electrical 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
UL RTI, Mechanical with Impact 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
UL RTI, Mechanical without Impact 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.850 mm		HB
@Thickness 0.0335 in		DAM; UL94
 HB
@Thickness 0.850 mm		HB
@Thickness 0.0335 in		DAM; IEC 60695-11-10
 
Processing PropertiesMetricEnglishComments
Melt Temperature 221 °C430 °F10°C/min; DAM; ISO 11357-1/-3
 270 °C518 °FDAM; Optimum
 260 - 280 °C500 - 536 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesWarp ResistantDAM
 Warpage, LowDAM
FillerMineral fillerDAM
FormsPelletsDAM
GenericNylon 6DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA6-MD40<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA6DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Warp ResinsDAM
 Mineral Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA6-MD40ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46724.html

免责声明: 本文 DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4