- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 1.4
- 弯曲模量 [MPa]: 11.1
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 50 % | 50 % | DAM | ||
| Water Absorption | 1.4 % @Temperature 23.0 °C | 1.4 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ASTM D570 | ||
| 1.4 % @Temperature 23.0 °C | 1.4 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62 | |||
| 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ASTM D570 | |||
| 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62 | |||
| Linear Mold Shrinkage, Flow | 0.0033 cm/cm @Thickness 2.00 mm | 0.0033 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm @Thickness 2.00 mm | 0.0058 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 233 MPa @Temperature 23.0 °C | 33800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 3.3 % @Temperature 23.0 °C | 3.3 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 12.0 GPa @Temperature 23.0 °C | 1740 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 15.5 GPa @Temperature 23.0 °C | 2250 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 11.1 GPa @Temperature 23.0 °C | 1610 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 14.3 GPa @Temperature 23.0 °C | 2070 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 9.80 J/cm² @Temperature 23.0 °C | 46.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 10.0 J/cm² @Temperature -30.0 °C | 47.6 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 11.0 J/cm² @Temperature -30.0 °C | 52.3 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| 2.10 J/cm² @Temperature -30.0 °C | 9.99 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 2.20 J/cm² @Temperature -30.0 °C | 10.5 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 9400 MPa @Temperature 23.0 °C | 1.36e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 7300 MPa @Temperature 23.0 °C | 1.06e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 5.00e+12 ohm @Temperature 23.0 °C | 5.00e+12 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| Comparative Tracking Index | 380 V @Temperature 23.0 °C | 380 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 219 °C | 426 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Heat Stabilized | DAM | |||
| Lubricated | DAM | ||||
| Filler | Glass fiber | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA6-GF50< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-GF50 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||