- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 0.297
- 硬度: 70.0
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | DAM; ASTM D792 | ||
| Density | 1.04 g/cc | 0.0376 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.5 % @Temperature 23.0 °C | 1.5 % @Temperature 73.4 °F | DAM; Immersion 24h; ASTM D570 | ||
| 2.3 % @Temperature 23.0 °C | 2.3 % @Temperature 73.4 °F | DAM; Equilibrium 50%RH; ISO 62, Similar to | |||
| 6.8 % @Temperature 23.0 °C | 6.8 % @Temperature 73.4 °F | DAM; Saturation, immersed; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.20 mm | 0.018 in/in @Thickness 0.126 in | DAM | ||
| 0.018 cm/cm @Thickness 2.00 mm | 0.018 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm @Thickness 3.20 mm | 0.018 in/in @Thickness 0.126 in | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 57 | 57 | 50%RH; ASTM D785 | ||
| Hardness, Rockwell R | 70 | 70 | 50%RH; ASTM D785 | ||
| Hardness, Shore D | 57 | 57 | 50%RH; ASTM D2240 | ||
| 70 | 70 | DAM; ASTM D2240 | |||
| Tensile Strength | 41.0 MPa @Temperature 23.0 °C | 5950 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 48.0 MPa @Temperature 23.0 °C | 6960 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Strength, Yield | 31.0 MPa @Temperature 23.0 °C | 4500 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 225 % @Temperature 23.0 °C | >= 225 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| >= 225 % @Temperature 23.0 °C | >= 225 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Yield | 29 % @Temperature 23.0 °C | 29 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 0.400 GPa @Temperature 23.0 °C | 58.0 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 0.900 GPa @Temperature 23.0 °C | 131 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 0.297 GPa @Temperature 23.0 °C | 43.1 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 0.524 GPa @Temperature 23.0 °C | 76.0 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Unnotched | 6.93 J/cm @Temperature -40.0 °C | 13.0 ft-lb/in @Temperature -40.0 °F | DAM; ASTM D256 | ||
| 8.00 J/cm @Temperature -20.0 °C | 15.0 ft-lb/in @Temperature -4.00 °F | DAM; ASTM D256 | |||
| 11.7 J/cm @Temperature 0.000 °C | 21.9 ft-lb/in @Temperature 32.0 °F | DAM; ASTM D256 | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ASTM D256 | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 7.10 J/cm² @Temperature 23.0 °C | 33.8 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 12.9 J/cm² @Temperature 23.0 °C | 61.4 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Impact Strength | 1310 kJ/m² @Temperature 23.0 °C | 623 ft-lb/in² @Temperature 73.4 °F | DAM; Long specimen; ASTM D1822 | ||
| 1363 kJ/m² @Temperature 23.0 °C | 648.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; Long specimen; ASTM D1822 | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM D696 | ||
| 200 µm/m-°C @Temperature 23.0 - 55.0 °C | 111 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 200 µm/m-°C @Temperature 23.0 - 55.0 °C | 111 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 180 µm/m-°C @Temperature 23.0 - 55.0 °C | 100 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 180 µm/m-°C @Temperature 23.0 - 55.0 °C | 100 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 216 °C | 421 °F | DAM; ASTM D3418 | ||
| 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DAM; ISO 75-1/-2 | ||
| 170 °C | 338 °F | DAM; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 | ||
| 52.0 °C | 126 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 95.0 °C @Thickness 0.750 mm | 203 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 100 °C @Thickness 1.50 mm | 212 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 °C | 464 °F | DAM; optimum; Extrusion | ||
| 235 - 250 °C | 455 - 482 °F | DAM; Extrusion | |||
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |||
| 270 °C | 518 °F | DAM; optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Dehumidified Dryer; Extrusion | |||
| Moisture Content | <= 0.060 % | <= 0.060 % | DAM; Extrusion | ||
| <= 0.060 % | <= 0.060 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | ||||
| Impact Modifier, Rubber | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | ||||
| Features | Elongation, Good | ||||
| Flexibility, Good | |||||
| Heat Aging Resistance, Good | |||||
| Heat Stabilized | |||||
| Impact Modified | |||||
| Impact Resistance, Good | |||||
| Lubricated | |||||
| Toughness, Good | |||||
| Forms | Pellets | ||||
| Generic | Nylon 6 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA6-HI< | ISO 11469 | |||
| Processing Method | Extrusion | ||||
| Product Category | Extrusion Resins | ||||
| Toughened Resins | |||||
| Unreinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA6-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Cable Jacketing | ||||
| Liners | |||||