- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 30.0
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | ISO 62 | ||
| Moisture Absorption | 0.700 % | 0.700 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 | 64 | conditioned, 15s; ISO 868 | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | dry; ISO 527-1/-2 | ||
| 60.0 MPa | 8700 psi | conditioned; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | dry; ISO 527-1/-2 | ||
| 30.0 MPa | 4350 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |||
| Elongation at Yield | 20 % | 20 % | conditioned; ISO 527-1/-2 | ||
| 20 % | 20 % | dry; ISO 527-1/-2 | |||
| Tensile Modulus | 0.500 GPa | 72.5 ksi | conditioned; ISO 527-1/-2 | ||
| 0.650 GPa | 94.3 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | dry; ISO 179/1eA | ||
| 4.00 J/cm² | 19.0 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 160 µm/m-°C | 88.9 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 174 °C | 345 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 80.0 - 110 °C | 176 - 230 °F | long term; EMS | ||
| 150 °C | 302 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Additives | Plasticizer | ||||
| Automotive | Powertrain and Chassis | ||||
| Electricals & Electronics | Cables & Tubes | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Processing | Other Extrusion | ||||
| Product Attributes | Flexible | ||||
| Improved friction & wear properties | |||||