- 密度 [g/cm3]: 1.03
- 拉伸强度 [MPa]: 33.0
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 21 % | 21 % | |
| Modulus of Elasticity | 0.700 GPa | 102 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | NB | NB | |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
| Surface Resistance | 5.00e+14 ohm | 5.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | |
| 9.0 @Frequency 100 Hz | 9.0 @Frequency 100 Hz | ||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | |
| Dissipation Factor | 0.075 @Frequency 1e+6 Hz | 0.075 @Frequency 1e+6 Hz | |
| 0.18 @Frequency 100 Hz | 0.18 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 µm/m-°C @Temperature 20.0 °C | <= 27.8 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
| Vicat Softening Point | 130 °C | 266 °F | 50°C/hr/50 N |