- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.35
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 1.47
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | at 23°C; ISO 62 | ||
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527 | ||
| 15.0 MPa @Temperature 120 °C | 2180 psi @Temperature 248 °F | ISO 527 | |||
| 22.0 MPa @Temperature 90.0 °C | 3190 psi @Temperature 194 °F | ISO 527 | |||
| 34.0 MPa @Temperature 60.0 °C | 4930 psi @Temperature 140 °F | ISO 527 | |||
| Flexural Modulus | 1.47 GPa | 213 ksi | ASTM D790 | ||
| 0.275 GPa @Temperature 120 °C | 39.9 ksi @Temperature 248 °F | ASTM D790 | |||
| 0.390 GPa @Temperature 90.0 °C | 56.6 ksi @Temperature 194 °F | ASTM D790 | |||
| 0.685 GPa @Temperature 60.0 °C | 99.4 ksi @Temperature 140 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.350 J/cm @Temperature -40.0 °C | 0.656 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.350 J/cm @Temperature -20.0 °C | 0.656 ft-lb/in @Temperature -4.00 °F | ASTM D256 | |||
| 0.450 J/cm @Temperature 23.0 °C | 0.843 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM D648 | ||
| Vicat Softening Point | 152 °C | 306 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Oxygen Index | 22 % | 22 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Heat Resistance - Ball Test (125°C) | Y | IEC 335 | |||
| Heat Resistance - Ball Test (165°C) | Y | IEC 335 | |||
| Injection Speed | medium - high | ||||
| Needle Burner Test | N | 1.47 mm | |||
| N | 3.05 mm | ||||