- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.1
- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 97.0
- 弯曲模量 [MPa]: 6.80
- 热变形温度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ATSM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 184 °C | 363 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |