- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 1.2
- 缺口冲击强度: 16.0
- 拉伸强度 [MPa]: 130.0
- 弯曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 1.2 % | 1.2 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F | ISO 11357 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous use |
| 145 °C | 293 °F | Short peaks operation | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |