- 密度 [g/cm3]: 1.64
- 缺口冲击强度: 1.12
- 弯曲模量 [MPa]: 13.12
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 149 MPa | 21600 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 16.06 GPa | 2329 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 13.12 GPa | 1903 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C @Thickness 3.20 mm | 345 °F @Thickness 0.126 in | unannealed; ASTM D648 |