- 密度 [g/cm3]: 1.17
- 缺口冲击强度: 0.48
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 109.0
- 热变形温度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.39 J/cm | 10.1 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 195 - 215 °C | 383 - 419 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |