DuPont Performance Polymers Zytel® 151L NC010 Nylon 612

DuPont Performance Polymers Zytel® 151L NC010 Nylon 612 物性表: DuPont Performance Polymers Zytel® 151L NC010 Nylon 612物性表及特性介绍,DuPont Performance Polymers Zytel® 151L NC010 Nylon 612注塑参数详情,如需DuPont Performance Polymers Zytel® 151L NC010 Nylon 612下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.06
  • 吸水率 [%]: 0.25
  • 成型收缩率 [%]: 0.011
  • 缺口冲击强度: 0.21
  • 拉伸强度 [MPa]: 30.0
  • 弯曲模量 [MPa]: 0.380
  • 硬度: 103.0
  • 热变形温度 [℃]: 135.0
  • 脆化温度 [℃]: -120.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.06 g/cc1.06 g/ccDAM; ASTM D792
Density 1.06 g/cc0.0383 lb/in³DAM; ISO 1183
Water Absorption  0.25 %
@Temperature 23.0 °C		0.25 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.3 %
@Temperature 23.0 °C		1.3 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.011 cm/cm
@Thickness 3.20 mm		0.011 in/in
@Thickness 0.126 in		Flow; DAM
 0.011 cm/cm
@Thickness 3.20 mm		0.011 in/in
@Thickness 0.126 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.013 cm/cm
@Thickness 2.00 mm		0.013 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 10310350%RH; ASTM D785
 114114DAM; ASTM D785
 114114DAM; ISO 2039/2
Tensile Strength  36.0 MPa
@Temperature 77.0 °C		5220 psi
@Temperature 171 °F		50%RH; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		DAM; ASTM D638
 52.0 MPa
@Temperature 23.0 °C		7540 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 93.0 MPa
@Temperature -40.0 °C		13500 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  9.39 MPa
@Strain 4.73 %,
Temperature 150 °C		1360 psi
@Strain 4.73 %,
Temperature 302 °F		DAM; ISO 527
 10.81 MPa
@Strain 0.420 %,
Temperature 23.0 °C		1568 psi
@Strain 0.420 %,
Temperature 73.4 °F		DAM; ISO 527
 13.32 MPa
@Strain 9.47 %,
Temperature 150 °C		1932 psi
@Strain 9.47 %,
Temperature 302 °F		DAM; ISO 527
 14.0 MPa
@Strain 0.530 %,
Temperature 0.000 °C		2030 psi
@Strain 0.530 %,
Temperature 32.0 °F		DAM; ISO 527
 14.94 MPa
@Strain 14.2 %,
Temperature 150 °C		2167 psi
@Strain 14.2 %,
Temperature 302 °F		DAM; ISO 527
 14.959 MPa
@Strain 4.585786 %,
Temperature 100 °C		2169.6 psi
@Strain 4.585786 %,
Temperature 212 °F		DAM; ISO 527
 15.75 MPa
@Strain 18.94 %,
Temperature 150 °C		2284 psi
@Strain 18.94 %,
Temperature 302 °F		DAM; ISO 527
 16.21 MPa
@Strain 23.67 %,
Temperature 150 °C		2351 psi
@Strain 23.67 %,
Temperature 302 °F		DAM; ISO 527
 16.65 MPa
@Strain 28.41 %,
Temperature 150 °C		2415 psi
@Strain 28.41 %,
Temperature 302 °F		DAM; ISO 527
 16.79 MPa
@Strain 33.14 %,
Temperature 150 °C		2435 psi
@Strain 33.14 %,
Temperature 302 °F		DAM; ISO 527
 16.98 MPa
@Strain 37.88 %,
Temperature 150 °C		2463 psi
@Strain 37.88 %,
Temperature 302 °F		DAM; ISO 527
 17.13 MPa
@Strain 42.61 %,
Temperature 150 °C		2485 psi
@Strain 42.61 %,
Temperature 302 °F		DAM; ISO 527
 17.32 MPa
@Strain 47.35 %,
Temperature 150 °C		2512 psi
@Strain 47.35 %,
Temperature 302 °F		DAM; ISO 527
 20.76 MPa
@Strain 0.850 %,
Temperature 23.0 °C		3011 psi
@Strain 0.850 %,
Temperature 73.4 °F		DAM; ISO 527
 21.563 MPa
@Strain 9.171572 %,
Temperature 100 °C		3127.5 psi
@Strain 9.171572 %,
Temperature 212 °F		DAM; ISO 527
 23.6 MPa
@Strain 0.860 %,
Temperature -40.0 °C		3420 psi
@Strain 0.860 %,
Temperature -40.0 °F		DAM; ISO 527
 24.603 MPa
@Strain 13.757358 %,
Temperature 100 °C		3568.4 psi
@Strain 13.757358 %,
Temperature 212 °F		DAM; ISO 527
 26.182 MPa
@Strain 18.343143 %,
Temperature 100 °C		3797.4 psi
@Strain 18.343143 %,
Temperature 212 °F		DAM; ISO 527
 27.052 MPa
@Strain 22.92893 %,
Temperature 100 °C		3923.6 psi
@Strain 22.92893 %,
Temperature 212 °F		DAM; ISO 527
 27.37 MPa
@Strain 1.06 %,
Temperature 0.000 °C		3970 psi
@Strain 1.06 %,
Temperature 32.0 °F		DAM; ISO 527
 27.581 MPa
@Strain 27.514715 %,
Temperature 100 °C		4000.3 psi
@Strain 27.514715 %,
Temperature 212 °F		DAM; ISO 527
 27.903 MPa
@Strain 32.100502 %,
Temperature 100 °C		4047.0 psi
@Strain 32.100502 %,
Temperature 212 °F		DAM; ISO 527
 28.088 MPa
@Strain 36.686287 %,
Temperature 100 °C		4073.8 psi
@Strain 36.686287 %,
Temperature 212 °F		DAM; ISO 527
 28.199 MPa
@Strain 41.272076 %,
Temperature 100 °C		4089.9 psi
@Strain 41.272076 %,
Temperature 212 °F		DAM; ISO 527
 28.416 MPa
@Strain 45.85786 %,
Temperature 100 °C		4121.4 psi
@Strain 45.85786 %,
Temperature 212 °F		DAM; ISO 527
 30.0 MPa
@Strain 1.27 %,
Temperature 23.0 °C		4350 psi
@Strain 1.27 %,
Temperature 73.4 °F		DAM; ISO 527
 38.66 MPa
@Strain 1.70 %,
Temperature 23.0 °C		5607 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 527
 39.91 MPa
@Strain 1.59 %,
Temperature 0.000 °C		5788 psi
@Strain 1.59 %,
Temperature 32.0 °F		DAM; ISO 527
 43.21 MPa
@Strain 1.72 %,
Temperature -40.0 °C		6267 psi
@Strain 1.72 %,
Temperature -40.0 °F		DAM; ISO 527
 46.54 MPa
@Strain 2.12 %,
Temperature 23.0 °C		6750 psi
@Strain 2.12 %,
Temperature 73.4 °F		DAM; ISO 527
 50.98 MPa
@Strain 2.12 %,
Temperature 0.000 °C		7394 psi
@Strain 2.12 %,
Temperature 32.0 °F		DAM; ISO 527
 52.93 MPa
@Strain 2.54 %,
Temperature 23.0 °C		7677 psi
@Strain 2.54 %,
Temperature 73.4 °F		DAM; ISO 527
 57.27 MPa
@Strain 2.97 %,
Temperature 23.0 °C		8306 psi
@Strain 2.97 %,
Temperature 73.4 °F		DAM; ISO 527
 59.69 MPa
@Strain 3.39 %,
Temperature 23.0 °C		8657 psi
@Strain 3.39 %,
Temperature 73.4 °F		DAM; ISO 527
 60.18 MPa
@Strain 2.65 %,
Temperature 0.000 °C		8728 psi
@Strain 2.65 %,
Temperature 32.0 °F		DAM; ISO 527
 60.87 MPa
@Strain 3.81 %,
Temperature 23.0 °C		8828 psi
@Strain 3.81 %,
Temperature 73.4 °F		DAM; ISO 527
 61.33 MPa
@Strain 4.24 %,
Temperature 23.0 °C		8895 psi
@Strain 4.24 %,
Temperature 73.4 °F		DAM; ISO 527
 61.62 MPa
@Strain 2.58 %,
Temperature -40.0 °C		8937 psi
@Strain 2.58 %,
Temperature -40.0 °F		DAM; ISO 527
 67.13 MPa
@Strain 3.18 %,
Temperature 0.000 °C		9736 psi
@Strain 3.18 %,
Temperature 32.0 °F		DAM; ISO 527
 71.79 MPa
@Strain 3.71 %,
Temperature 0.000 °C		10410 psi
@Strain 3.71 %,
Temperature 32.0 °F		DAM; ISO 527
 74.36 MPa
@Strain 4.24 %,
Temperature 0.000 °C		10790 psi
@Strain 4.24 %,
Temperature 32.0 °F		DAM; ISO 527
 75.37 MPa
@Strain 3.44 %,
Temperature -40.0 °C		10930 psi
@Strain 3.44 %,
Temperature -40.0 °F		DAM; ISO 527
 75.4 MPa
@Strain 4.77 %,
Temperature 0.000 °C		10900 psi
@Strain 4.77 %,
Temperature 32.0 °F		DAM; ISO 527
 75.89 MPa
@Strain 5.30 %,
Temperature 0.000 °C		11010 psi
@Strain 5.30 %,
Temperature 32.0 °F		DAM; ISO 527
 85.21 MPa
@Strain 4.30 %,
Temperature -40.0 °C		12360 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 527
 91.26 MPa
@Strain 5.16 %,
Temperature -40.0 °C		13240 psi
@Strain 5.16 %,
Temperature -40.0 °F		DAM; ISO 527
 94.56 MPa
@Strain 6.02 %,
Temperature -40.0 °C		13710 psi
@Strain 6.02 %,
Temperature -40.0 °F		DAM; ISO 527
 96.28 MPa
@Strain 6.88 %,
Temperature -40.0 °C		13960 psi
@Strain 6.88 %,
Temperature -40.0 °F		DAM; ISO 527
 96.88 MPa
@Strain 7.74 %,
Temperature -40.0 °C		14050 psi
@Strain 7.74 %,
Temperature -40.0 °F		DAM; ISO 527
 97.17 MPa
@Strain 8.60 %,
Temperature -40.0 °C		14090 psi
@Strain 8.60 %,
Temperature -40.0 °F		DAM; ISO 527
Tensile Strength, Yield  30.0 MPa
@Temperature 77.0 °C		4350 psi
@Temperature 171 °F		DAM; ASTM D638
 35.0 MPa
@Temperature 77.0 °C		5080 psi
@Temperature 171 °F		50%RH; ASTM D638
 51.0 MPa
@Temperature 23.0 °C		7400 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 54.0 MPa
@Temperature 23.0 °C		7830 psi
@Temperature 73.4 °F		50%RH; ISO 527
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 62.0 MPa
@Temperature 23.0 °C		8990 psi
@Temperature 73.4 °F		DAM; ISO 527
 93.0 MPa
@Temperature -40.0 °C		13500 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  10 %
@Temperature -40.0 °C		10 %
@Temperature -40.0 °F		DAM; ASTM D638
 17 %
@Temperature 23.0 °C		17 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 20 %
@Temperature -40.0 °C		20 %
@Temperature -40.0 °F		50%RH; ASTM D638
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 100 %
@Temperature 23.0 °C		100 %
@Temperature 73.4 °F		DAM; ASTM D638
 230 %
@Temperature 77.0 °C		230 %
@Temperature 171 °F		DAM; ASTM D638
 250 %
@Temperature 23.0 °C		250 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		50%RH; ASTM D638
Elongation at Yield  4.5 %
@Temperature 23.0 °C		4.5 %
@Temperature 73.4 °F		DAM; ISO 527
 7.0 %
@Temperature 23.0 °C		7.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 8.0 %
@Temperature -40.0 °C		8.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 10 %
@Temperature -40.0 °C		10 %
@Temperature -40.0 °F		50%RH; ASTM D638
 18 %
@Temperature 23.0 °C		18 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 23.0 °C		30 %
@Temperature 73.4 °F		50%RH; ASTM D638
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 40 %
@Temperature 77.0 °C		40 %
@Temperature 171 °F		50%RH; ASTM D638
Tensile Modulus  1.70 GPa
@Temperature 23.0 °C		247 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 2.40 GPa
@Temperature 23.0 °C		348 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.380 GPa
@Temperature 77.0 °C		55.1 ksi
@Temperature 171 °F		50%RH; ASTM D790
 0.410 GPa
@Temperature 77.0 °C		59.5 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.24 GPa
@Temperature 23.0 °C		180 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 1.44 GPa
@Temperature 23.0 °C		209 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 2.03 GPa
@Temperature 23.0 °C		294 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 2.10 GPa
@Temperature 23.0 °C		305 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.34 GPa
@Temperature -40.0 °C		339 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 2.76 GPa
@Temperature -40.0 °C		400 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Modulus  0.00100 GPa
@Temperature 218 °C		0.145 ksi
@Temperature 424 °F		DAM; ISO 6721
 0.0200 GPa
@Temperature 210 °C		2.90 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.0340 GPa
@Temperature 204 °C		4.93 ksi
@Temperature 399 °F		DAM; ISO 6721
 0.0420 GPa
@Temperature 200 °C		6.09 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.0540 GPa
@Temperature 194 °C		7.83 ksi
@Temperature 381 °F		DAM; ISO 6721
 0.0610 GPa
@Temperature 190 °C		8.85 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.0760 GPa
@Temperature 180 °C		11.0 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.0870 GPa
@Temperature 170 °C		12.6 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.0950 GPa
@Temperature 160 °C		13.8 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.100 GPa
@Temperature 150 °C		14.5 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.105 GPa
@Temperature 140 °C		15.2 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.111 GPa
@Temperature 130 °C		16.1 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.117 GPa
@Temperature 120 °C		17.0 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.123 GPa
@Temperature 110 °C		17.8 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.131 GPa
@Temperature 100 °C		19.0 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.141 GPa
@Temperature 90.0 °C		20.5 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.156 GPa
@Temperature 80.0 °C		22.6 ksi
@Temperature 176 °F		DAM; ISO 6721
 0.182 GPa
@Temperature 70.0 °C		26.4 ksi
@Temperature 158 °F		DAM; ISO 6721
 0.235 GPa
@Temperature 60.0 °C		34.1 ksi
@Temperature 140 °F		DAM; ISO 6721
 0.403 GPa
@Temperature 50.0 °C		58.5 ksi
@Temperature 122 °F		DAM; ISO 6721
 0.571 GPa
@Temperature 40.0 °C		82.8 ksi
@Temperature 104 °F		DAM; ISO 6721
 0.679 GPa
@Temperature 30.0 °C		98.5 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 0.726 GPa
@Temperature 20.0 °C		105 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 0.748 GPa
@Temperature 10.0 °C		108 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 0.761 GPa
@Temperature 0.000 °C		110 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 0.770 GPa
@Temperature -10.0 °C		112 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 0.778 GPa
@Temperature -20.0 °C		113 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 0.787 GPa
@Temperature -30.0 °C		114 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 0.801 GPa
@Temperature -40.0 °C		116 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 0.828 GPa
@Temperature -50.0 °C		120 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Shear Strength 58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.210 J/cm
@Temperature -40.0 °C		0.393 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.430 J/cm
@Temperature 23.0 °C		0.806 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.690 J/cm
@Temperature 23.0 °C		1.29 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  3.00 kJ/m²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.350 J/cm²
@Temperature 23.0 °C		1.67 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.350 J/cm²
@Temperature -30.0 °C		1.67 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.400 J/cm²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
Surface Resistance 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 5.1
@Frequency 100 Hz,
Temperature 23.0 °C		5.1
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 7.10 kV/mm
@Temperature 93.0 °C		180 kV/in
@Temperature 199 °F		DAM; Short Time; ASTM D149
 14.2 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		361 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
 21.2 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		538 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		50%RH; IEC 60243-1
 21.9 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		556 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.0135
@Frequency 100 Hz,
Temperature 23.0 °C		0.0135
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.016
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.016
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 100 Hz,
Temperature 23.0 °C		0.020
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.040
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.040
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.070
@Frequency 100 Hz,
Temperature 23.0 °C		0.070
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.15
@Frequency 100 Hz,
Temperature 23.0 °C		0.15
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.15
@Frequency 1000 Hz,
Temperature 23.0 °C		0.15
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; ASTM D3638
 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		50.0 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 180 µm/m-°C
@Temperature 55.0 - 160 °C		100 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 218 °C424 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 135 °C275 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C131 °FDAM; ASTM D648
 62.0 °C144 °FDAM; ISO 75-1/-2
Brittleness Temperature -120 °C-184 °FDAM; ASTM D746
 -107 °C-161 °F50%RH; ASTM D746
UL RTI, Electrical  105 °C
@Thickness 0.860 mm		221 °F
@Thickness 0.0339 in		DAM; UL 746B
 105 °C
@Thickness 1.50 mm		221 °F
@Thickness 0.0591 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
Flammability, UL94  V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.860 mm		V-2
@Thickness 0.0339 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.860 mm		V-2
@Thickness 0.0339 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; UL94
Oxygen Index 27 %27 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 218 °C424 °F10°C/min; DAM; ISO 11357-1/-3
 250 °C482 °FDAM; Optimum
 230 - 290 °C446 - 554 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.15 %<= 0.15 %DAM
 
Descriptive Properties
AdditiveLubricantDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Dimensional Stability, GoodDAM
 LubricatedDAM
 Moisture Absorption, LowDAM
FormsPelletsDAM
GenericNylon 612DAM
Material StatusCurrentDAM
Part Marking Code>PA612<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA612DAM
Processing MethodInjection MoldingDAM
Product CategoryUnreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA612ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesElectrical/Electronic ApplicationsDAM
 GearsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47473.html

免责声明: 本文 DuPont Performance Polymers Zytel® 151L NC010 Nylon 612 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4