- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 1.38
- 弯曲模量 [MPa]: 7.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec | 0.0020 in/in @Time 24.0 hour | ASTM D955 |
| 0.0024 cm/cm @Time 86400 sec | 0.0024 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| 0.0084 cm/cm @Time 86400 sec | 0.0084 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 154 MPa | 22300 psi | ASTM D638 |
| 157 MPa | 22800 psi | ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Tensile Modulus | 9.96 GPa | 1440 ksi | 50 mm/min; ASTM D638 |
| 10.31 GPa | 1495 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 231 MPa | 33500 psi | ISO 178 |
| 241 MPa | 35000 psi | ASTM D790 | |
| Flexural Modulus | 7.92 GPa | 1150 ksi | ISO 178 |
| 8.61 GPa | 1250 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.69 J/cm | 21.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 14.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 26.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 14.6 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 75.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 42.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 76.9 µm/m-°C @Temperature -40.0 - 40.0 °C | 42.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |