- 密度 [g/cm3]: 1.04
- 弯曲模量 [MPa]: 0.530
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 Type 1A |
| Elongation at Break | 240 % | 240 % | ISO 527 Type 1A |
| Tensile Modulus | 0.550 GPa | 79.8 ksi | ISO 527 Type 1A |
| Flexural Strength | 22.0 MPa | 3190 psi | ISO 178 |
| Flexural Modulus | 0.530 GPa | 76.9 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 11.7 J/cm² @Temperature 23.0 °C | 55.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 215 °C | 419 °F | ISO 11357 |
| Moisture Content | <= 0.10 % | <= 0.10 % | |