- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 0.37
- 弯曲模量 [MPa]: 5.99
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.44 g/cc | 0.0520 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.13 % @Time 86400 sec | 0.13 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D 638 |
| 126 MPa | 18300 psi | ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 |
| 2.5 % | 2.5 % | ASTM D 638 | |
| Tensile Modulus | 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D 638 |
| 9.58 GPa | 1390 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 171 MPa | 24800 psi | ASTM D 790 |
| 185 MPa | 26800 psi | ISO 178 | |
| Flexural Modulus | 5.99 GPa | 869 ksi | ASTM D 790 |
| 7.01 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C | 0.693 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 3.79 J/cm @Temperature 23.0 °C | 7.10 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C | 13.8 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.37 | 0.37 | ASTM D 3702 Modified |
| K (wear) Factor | 127 x 10-8 mm³/N-M | 63.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1000 - 100000 ohm-cm | 1000 - 100000 ohm-cm | ASTM D 257 |
| Surface Resistance | 1000 - 100000 ohm | 1000 - 100000 ohm | ASTM D 257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 164 °C @Thickness 3.20 mm | 327 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 by SABIC-IP |