- 密度 [g/cm3]: 1.41
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 118.0
- 断裂伸长率 [%]: 165
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 12.8 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 60.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL 94 |