- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.95
- 拉伸强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.080 % | 0.080 % | 24 Hours; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 260 MPa | 37700 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.950 J/cm | 1.78 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 60 Hz | 2.9 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 60 Hz | 0.0030 @Frequency 60 Hz | ASTM D150 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 °C | 7.22 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Use; UL-746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ASTM D648 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 |
| Oxygen Index | 45 % | 45 % | Limiting; ASTM D2863 |