PA6 BG3 15%玻璃注射成型、_产品资讯

PA6 BG3 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.23 g/cc	0.0444 lb/in³	ISO 1183
Water Absorption at Saturation	8.0 % @Temperature 23.0 °C	8.0 % @Temperature 73.4 °F	ISO 62-1
Linear Mold Shrinkage, Flow	0.0045 - 0.0085 cm/cm	0.0045 - 0.0085 in/in	on Tensile Bar; ISO 294

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	110	110	ISO 2039-2
Tensile Strength at Break	125 MPa	18100 psi	5 mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5 mm/min; ISO 527
Tensile Modulus	5.80 GPa	841 ksi	1 mm/min; ISO 527
Flexural Strength	180 MPa	26100 psi	break, 2 mm/min; ISO 178
Flexural Modulus	4.75 GPa	689 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	35.0 kJ/m² @Temperature -30.0 °C	16.7 ft-lb/in² @Temperature -22.0 °F	80x10x4; ISO 180/1U
	40.0 kJ/m² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	80x10x4; ISO 180/1U
Charpy Impact Unnotched	4.50 J/cm²	21.4 ft-lb/in²	Edgew 80x10x4 sp=62; ISO 179/1eU

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	ROA; IEC 60093
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz	3.4 @Frequency 1.00e+6 Hz	IEC 60250
	3.6 @Frequency 50.0 - 60.0 Hz	3.6 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	20.0 kV/mm @Thickness 3.20 mm	508 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor	0.0061 @Frequency 50.0 - 60.0 Hz	0.0061 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.016 @Frequency 1.00e+6 Hz	0.016 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	M; IEC 60112
	550 V	550 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C @Temperature 23.0 - 60.0 °C	27.8 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature 23.0 - 60.0 °C	55.6 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	212 °C	414 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point	206 °C	403 °F	B/120; ISO 306
UL RTI, Electrical	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
Oxygen Index	24 %	24 %	ISO 4589

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	230 - 240 °C	446 - 464 °F	Zone 1
Middle Barrel Temperature	240 - 250 °C	464 - 482 °F	Zone 2
Front Barrel Temperature	240 - 270 °C	464 - 518 °F	Zone 3
Melt Temperature	240 - 270 °C	464 - 518 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	75.0 - 85.0 °C	167 - 185 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

PA6 BG3 15%玻璃 注射成型、

PA6 BG3 15%玻璃注射成型、