类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋，品位的影响
材料说明：超级增韧高粘度缩醛均聚物
聚甲醛第一百bk602是超韧高粘度缩醛均聚物级耐冲击性优良。它是专为高度强调的部分，突出的韧性是必不可少的。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 2577 | ||
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 30 % | 30 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 | ||
| Shear Modulus | 0.0351 GPa @Temperature 160 °C |
5.09 ksi @Temperature 320 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.0816 GPa @Temperature 120 °C |
11.8 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.1884 GPa @Temperature 70.0 °C |
27.33 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.3691 GPa @Temperature 20.0 °C |
53.53 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.5982 GPa @Temperature -20.0 °C |
86.76 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.1904 GPa @Temperature -50.0 °C |
172.66 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eA | ||
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Emissions | <8 mg/kg | VDA 275 | |||
| Part Marking Code | >POM-HI< | ISO 11469 | |||
| Processing | Blow Moulding | ||||
| Coatable | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-HI | ISO 1043 | |||
| UL recognition | UL | ||||