  4. 杜邦高性能聚合物聚甲醛POM 100T NC010 乙缩醛

杜邦高性能聚合物聚甲醛POM 100T NC010 乙缩醛

POM 100T NC010材料说明：增韧高粘度缩醛均聚物 Delrin 100T NC010是增韧高粘度缩醛均聚物具有高抗冲击级。
 杜邦高性能聚合物聚甲醛（POM）®100T NC010乙缩醛
类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋，品位的影响
材料说明：增韧高粘度缩醛均聚物
Delrin 100T NC010是增韧高粘度缩醛均聚物具有高抗冲击级。
物性表：

 
Physical Properties Metric English Comments
Density  1.37 g/cc 0.0495 lb/in³ ISO 1183
Water Absorption  0.90 %
@Thickness 2.00 mm		 0.90 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.300 %
@Thickness 2.00 mm		 0.300 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   165000 cP
@Shear Rate 5000 1/s,
Temperature 220 °C		 165000 cP
@Shear Rate 5000 1/s,
Temperature 428 °F		 ISO 11403-1 -2
  187000 cP
@Shear Rate 5000 1/s,
Temperature 205 °C		 187000 cP
@Shear Rate 5000 1/s,
Temperature 401 °F		 ISO 11403-1 -2
  214000 cP
@Shear Rate 5000 1/s,
Temperature 190 °C		 214000 cP
@Shear Rate 5000 1/s,
Temperature 374 °F		 ISO 11403-1 -2
  781000 cP
@Shear Rate 500 1/s,
Temperature 220 °C		 781000 cP
@Shear Rate 500 1/s,
Temperature 428 °F		 ISO 11403-1 -2
  917000 cP
@Shear Rate 500 1/s,
Temperature 205 °C		 917000 cP
@Shear Rate 500 1/s,
Temperature 401 °F		 ISO 11403-1 -2
  1.082e+6 cP
@Shear Rate 500 1/s,
Temperature 190 °C		 1.082e+6 cP
@Shear Rate 500 1/s,
Temperature 374 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.015 cm/cm 0.015 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow   2.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 2.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  2.1 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 2.1 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  59 59 ISO 2039-2
Hardness, Rockwell R  113 113 ISO 2039-2
Tensile Stress   8.50 MPa
@Strain 1.60 %,
Temperature 90.0 °C		 1230 psi
@Strain 1.60 %,
Temperature 194 °F		 ISO 11403-1 -2
  19.3 MPa
@Strain 6.50 %,
Temperature 90.0 °C		 2800 psi
@Strain 6.50 %,
Temperature 194 °F		 ISO 11403-1 -2
  22.0 MPa
@Strain 1.90 %,
Temperature 40.0 °C		 3190 psi
@Strain 1.90 %,
Temperature 104 °F		 ISO 11403-1 -2
  22.9 MPa
@Strain 11.4 %,
Temperature 90.0 °C		 3320 psi
@Strain 11.4 %,
Temperature 194 °F		 ISO 11403-1 -2
  23.7 MPa
@Strain 16.3 %,
Temperature 90.0 °C		 3440 psi
@Strain 16.3 %,
Temperature 194 °F		 ISO 11403-1 -2
  29.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		 4210 psi
@Strain 2.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  36.0 MPa
@Strain 2.60 %,
Temperature 0.000 °C		 5220 psi
@Strain 2.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  40.0 MPa
@Strain 7.60 %,
Temperature 40.0 °C		 5800 psi
@Strain 7.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  40.0 MPa
@Strain 2.30 %,
Temperature -20.0 °C		 5800 psi
@Strain 2.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  44.0 MPa
@Strain 13.3 %,
Temperature 40.0 °C		 6380 psi
@Strain 13.3 %,
Temperature 104 °F		 ISO 11403-1 -2
  44.7 MPa
@Strain 21.0 %,
Temperature 40.0 °C		 6480 psi
@Strain 21.0 %,
Temperature 104 °F		 ISO 11403-1 -2
  48.7 MPa
@Strain 10.2 %,
Temperature 23.0 °C		 7060 psi
@Strain 10.2 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  50.9 MPa
@Strain 17.8 %,
Temperature 23.0 °C		 7380 psi
@Strain 17.8 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  51.2 MPa
@Strain 25.4 %,
Temperature 23.0 °C		 7430 psi
@Strain 25.4 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  56.1 MPa
@Strain 10.6 %,
Temperature 0.000 °C		 8140 psi
@Strain 10.6 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  58.3 MPa
@Strain 18.5 %,
Temperature 0.000 °C		 8460 psi
@Strain 18.5 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  58.6 MPa
@Strain 26.4 %,
Temperature 0.000 °C		 8500 psi
@Strain 26.4 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  63.9 MPa
@Strain 9.20 %,
Temperature -20.0 °C		 9270 psi
@Strain 9.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  67.0 MPa
@Strain 16.2 %,
Temperature -20.0 °C		 9720 psi
@Strain 16.2 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  67.8 MPa
@Strain 23.1 %,
Temperature -20.0 °C		 9830 psi
@Strain 23.1 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Tensile Strength, Yield  55.0 MPa 7980 psi ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % Nominal; ISO 527-1/-2
Elongation at Yield  25 % 25 % ISO 527-1/-2
Tensile Modulus  1.90 GPa 276 ksi ISO 527-1/-2
Flexural Modulus  1.70 GPa 247 ksi ISO 178
Shear Modulus   0.115 GPa
@Temperature 120 °C		 16.7 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.262 GPa
@Temperature 70.0 °C		 38.0 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.514 GPa
@Temperature 20.0 °C		 74.6 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  0.729 GPa
@Temperature -20.0 °C		 106 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.166 GPa
@Temperature -50.0 °C		 169.1 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.252 GPa
@Strain 20.3 %,
Temperature 23.0 °C		 36.5 ksi
@Strain 20.3 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.277 GPa
@Strain 21.1 %,
Temperature 0.000 °C		 40.2 ksi
@Strain 21.1 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.293 GPa
@Strain 15.2 %,
Temperature 40.0 °C		 42.5 ksi
@Strain 15.2 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.365 GPa
@Strain 18.5 %,
Temperature -20.0 °C		 52.9 ksi
@Strain 18.5 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.477 GPa
@Strain 10.2 %,
Temperature 23.0 °C		 69.2 ksi
@Strain 10.2 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.526 GPa
@Strain 7.60 %,
Temperature 40.0 °C		 76.3 ksi
@Strain 7.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.529 GPa
@Strain 10.6 %,
Temperature 0.000 °C		 76.8 ksi
@Strain 10.6 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.695 GPa
@Strain 9.20 %,
Temperature -20.0 °C		 101 ksi
@Strain 9.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.16 GPa
@Strain 1.90 %,
Temperature 40.0 °C		 168 ksi
@Strain 1.90 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.16 GPa
@Strain 2.50 %,
Temperature 23.0 °C		 168 ksi
@Strain 2.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.38 GPa
@Strain 2.60 %,
Temperature 0.000 °C		 201 ksi
@Strain 2.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.74 GPa
@Strain 2.30 %,
Temperature -20.0 °C		 252 ksi
@Strain 2.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  2.50 J/cm² 11.9 ft-lb/in² ISO 179/1eA
  1.30 J/cm²
@Temperature -30.0 °C		 6.19 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  130 °C 266 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  72.0 °C 162 °F ISO 75-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM-I< ISO 11469
Processing Blow Moulding  
  Coatable  
  Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM-I ISO 1043
UL recognition UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38468.html

免责声明: 本文 杜邦高性能聚合物聚甲醛POM 100T NC010 乙缩醛 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4