LCP V400P 材料说明：共挤出LCP屏障的应用。v400p Vectra液晶聚合物具有优良的阻隔性能，独立的相对湿度，耐化学性和薄膜应用接触清晰。这种材料不适合用于医疗或牙科植入物。
LCP V400P 形式：颗粒状
LCP V400P 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C/50%RH; ISO 62 |
| Moisture Vapor Transmission | 0.0100 cc-mm/m²-24hr-atm @Temperature 38.0 °C |
0.0254 cc-mil/100 in²-24hr-atm @Temperature 100 °F |
DIN 53122 |
| Water Vapor Transmission | 0.0300 g/m²/day | 0.00193 g/100 in²/day | DIN 53122-2 |
| Oxygen Transmission | 0.03175 cc-mm/m²-24hr-atm | 0.08065 cc-mil/100 in²-24hr-atm | 100%RH; DIN 53380 part 3 |
| 0.03375 cc-mm/m²-24hr-atm | 0.08573 cc-mil/100 in²-24hr-atm | 0%RH; DIN 53380 part 3 | |
| 0.0800 cc-mm/m²-24hr-atm | 0.203 cc-mil/100 in²-24hr-atm | 100%RH; DIN 53380 part 3 | |
| 0.0900 cc-mm/m²-24hr-atm | 0.229 cc-mil/100 in²-24hr-atm | 0% RH; DIN 53380 part 3 | |
| Melt Index of Compound | 14.0 g/10 min @Temperature 230 °C |
14.0 g/10 min @Temperature 446 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 151 MPa | 21900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.62 % | 1.62 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.4 GPa | 2090 ksi | 50mm/min; ISO 527-2/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 110 °C | 230 °F | onset; ISO 3146 |