  4. 杜邦高性能聚合物lw9030fr NC010低翘曲30%玻纤

杜邦高性能聚合物lw9030fr NC010低翘曲30%玻纤

杜邦高性能聚合物Crastin®lw9030fr NC010PBT的+ASA 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；PBT + ASA共混，玻璃纤维增强 材料说明：低翘曲的特点增强阻燃聚对苯二甲酸丁二醇酯共混物30%玻璃 Crastin lw9030fr NC010是30%玻璃纤维增强阻燃聚对苯二甲酸丁二醇酯共混物注射成型。
 物性表：

 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³  
  1.57 g/cc 0.0567 lb/in³ ISO 1183
Water Absorption  0.72 %
@Thickness 2.00 mm		 0.72 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.210 %
@Thickness 2.00 mm		 0.210 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  125 MPa 18100 psi ISO 527-1/-2
Tensile Stress   4.04 MPa
@Strain 0.200 %,
Temperature 150 °C		 586 psi
@Strain 0.200 %,
Temperature 302 °F		 ISO 11403-1 -2
  5.165 MPa
@Strain 0.310 %,
Temperature 160 °C		 749.1 psi
@Strain 0.310 %,
Temperature 320 °F		 ISO 11403-1 -2
  12.8 MPa
@Strain 0.940 %,
Temperature 150 °C		 1860 psi
@Strain 0.940 %,
Temperature 302 °F		 ISO 11403-1 -2
  15.5 MPa
@Strain 1.48 %,
Temperature 150 °C		 2250 psi
@Strain 1.48 %,
Temperature 302 °F		 ISO 11403-1 -2
  17.14 MPa
@Strain 2.03 %,
Temperature 150 °C		 2486 psi
@Strain 2.03 %,
Temperature 302 °F		 ISO 11403-1 -2
  17.37 MPa
@Strain 2.935 %,
Temperature 160 °C		 2519 psi
@Strain 2.935 %,
Temperature 320 °F		 ISO 11403-1 -2
  34.95 MPa
@Strain 0.400 %,
Temperature 40.0 °C		 5069 psi
@Strain 0.400 %,
Temperature 104 °F		 ISO 11403-1 -2
  36.17 MPa
@Strain 0.340 %,
Temperature 23.0 °C		 5246 psi
@Strain 0.340 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  42.12 MPa
@Strain 0.850 %,
Temperature 90.0 °C		 6109 psi
@Strain 0.850 %,
Temperature 194 °F		 ISO 11403-1 -2
  50.29 MPa
@Strain 1.21 %,
Temperature 90.0 °C		 7294 psi
@Strain 1.21 %,
Temperature 194 °F		 ISO 11403-1 -2
  55.1 MPa
@Strain 1.57 %,
Temperature 90.0 °C		 7990 psi
@Strain 1.57 %,
Temperature 194 °F		 ISO 11403-1 -2
  58.12 MPa
@Strain 1.92 %,
Temperature 90.0 °C		 8430 psi
@Strain 1.92 %,
Temperature 194 °F		 ISO 11403-1 -2
  60.34 MPa
@Strain 0.580 %,
Temperature 0.000 °C		 8752 psi
@Strain 0.580 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  74.31 MPa
@Strain 0.710 %,
Temperature -20.0 °C		 10780 psi
@Strain 0.710 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  75.6 MPa
@Strain 1.05 %,
Temperature 40.0 °C		 11000 psi
@Strain 1.05 %,
Temperature 104 °F		 ISO 11403-1 -2
  77.91 MPa
@Strain 0.770 %,
Temperature 0.000 °C		 11300 psi
@Strain 0.770 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  87.45 MPa
@Strain 0.960 %,
Temperature 23.0 °C		 12680 psi
@Strain 0.960 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  87.68 MPa
@Strain 1.37 %,
Temperature 40.0 °C		 12720 psi
@Strain 1.37 %,
Temperature 104 °F		 ISO 11403-1 -2
  96.93 MPa
@Strain 0.960 %,
Temperature -20.0 °C		 14060 psi
@Strain 0.960 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  96.94 MPa
@Strain 1.77 %,
Temperature 40.0 °C		 14060 psi
@Strain 1.77 %,
Temperature 104 °F		 ISO 11403-1 -2
  98.11 MPa
@Strain 1.03 %,
Temperature 0.000 °C		 14230 psi
@Strain 1.03 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  105.41 MPa
@Strain 1.30 %,
Temperature 23.0 °C		 15288 psi
@Strain 1.30 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  110.94 MPa
@Strain 1.22 %,
Temperature 0.000 °C		 16091 psi
@Strain 1.22 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  114.82 MPa
@Strain 1.57 %,
Temperature 23.0 °C		 16653 psi
@Strain 1.57 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  120.22 MPa
@Strain 1.28 %,
Temperature -20.0 °C		 17436 psi
@Strain 1.28 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Elongation at Break  1.8 % 1.8 % ISO 527-1/-2
Tensile Modulus  10.5 GPa 1520 ksi ISO 527-1/-2
  1.856 GPa
@Temperature 150 °C		 269.2 ksi
@Temperature 302 °F		 ISO 11403-1 -2
  7.46 GPa
@Temperature 60.0 °C		 1080 ksi
@Temperature 140 °F		 ISO 11403-1 -2
  11.243 GPa
@Temperature -20.0 °C		 1630.7 ksi
@Temperature -4.00 °F		 ISO 11403-1 -2
Flexural Strength  175 MPa 25400 psi ISO 178
Secant Modulus   2.275 GPa
@Strain 2.00 %,
Temperature 100 °C		 330.0 ksi
@Strain 2.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  2.756 GPa
@Strain 2.50 %,
Temperature 80.0 °C		 399.7 ksi
@Strain 2.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  4.40 GPa
@Strain 0.250 %,
Temperature 100 °C		 638 ksi
@Strain 0.250 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.94 GPa
@Strain 1.00 %,
Temperature 80.0 °C		 716 ksi
@Strain 1.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  5.14 GPa
@Strain 1.93 %,
Temperature 40.0 °C		 746 ksi
@Strain 1.93 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.02 GPa
@Strain 1.53 %,
Temperature 40.0 °C		 872 ksi
@Strain 1.53 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.89 GPa
@Strain 1.71 %,
Temperature 23.0 °C		 1000 ksi
@Strain 1.71 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  7.20 GPa
@Strain 1.05 %,
Temperature 40.0 °C		 1040 ksi
@Strain 1.05 %,
Temperature 104 °F		 ISO 11403-1 -2
  7.9073 GPa
@Strain 1.37 %,
Temperature 23.0 °C		 1146.9 ksi
@Strain 1.37 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.7375 GPa
@Strain 0.400 %,
Temperature 40.0 °C		 1267.3 ksi
@Strain 0.400 %,
Temperature 104 °F		 ISO 11403-1 -2
  8.75 GPa
@Strain 1.60 %,
Temperature -20.0 °C		 1270 ksi
@Strain 1.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  8.77 GPa
@Strain 1.35 %,
Temperature 0.000 °C		 1270 ksi
@Strain 1.35 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.11 GPa
@Strain 0.960 %,
Temperature 23.0 °C		 1320 ksi
@Strain 0.960 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  9.37 GPa
@Strain 1.10 %,
Temperature 0.000 °C		 1360 ksi
@Strain 1.10 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.1 GPa
@Strain 0.960 %,
Temperature -20.0 °C		 1460 ksi
@Strain 0.960 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.1 GPa
@Strain 0.770 %,
Temperature 0.000 °C		 1470 ksi
@Strain 0.770 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.4 GPa
@Strain 0.580 %,
Temperature 0.000 °C		 1510 ksi
@Strain 0.580 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.5 GPa
@Strain 0.710 %,
Temperature -20.0 °C		 1520 ksi
@Strain 0.710 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.6 GPa
@Strain 0.340 %,
Temperature 23.0 °C		 1540 ksi
@Strain 0.340 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  7.00 kJ/m² 3.33 ft-lb/in² ISO 180/1A
  7.00 kJ/m²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  35.0 kJ/m² 16.7 ft-lb/in² ISO 180/1U
  35.0 kJ/m²
@Temperature -30.0 °C		 16.7 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² ISO 179/1eA
  0.800 J/cm²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  9500 MPa
@Time 3600 sec		 1.38e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  7400 MPa
@Time 3.60e+6 sec		 1.07e+6 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 60093
Dielectric Constant   3.6
@Frequency 1.00e+6 Hz		 3.6
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  28.0 kV/mm 711 kV/in IEC 60243-1
  20.0 kV/mm
@Thickness 2.00 mm		 508 kV/in
@Thickness 0.0787 in		 20s; IEC 60243-1
  28.0 kV/mm
@Thickness 1.00 mm		 711 kV/in
@Thickness 0.0394 in		 Short Time; IEC 60243-1
Dissipation Factor   0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 IEC 60250
  0.015
@Frequency 1.00e+6 Hz		 0.015
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  400 V 400 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  25.0 µm/m-°C 13.9 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  80.0 µm/m-°C 44.4 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.85 J/g-°C 0.442 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  190 °C 374 °F ISO 75-1/-2
Vicat Softening Point  150 °C 302 °F 50°C/h 50N; ISO 306
Flammability, UL94   V-0
@Thickness 1.50 mm		 V-0
@Thickness 0.0591 in		 IEC 60695-11-10
  V-0
@Thickness 0.800 mm		 V-0
@Thickness 0.0315 in		 IEC 60695-11-10
  5VA
@Thickness 3.00 mm		 5VA
@Thickness 0.118 in		 IEC 60695-11-20
Oxygen Index  27 % 27 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT+ASA-GF30FR(17)< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT+ASA-GF30FR(17)  
UL recognition UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40870.html

免责声明: 本文 杜邦高性能聚合物lw9030fr NC010低翘曲30%玻纤 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4