| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Viscosity | 160000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
160000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
melt viscosity; b.o. ISO 11443-A |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Melt Flow | 28.32 g/10 min @Load 0.510 kg, Temperature 240 °C |
28.32 g/10 min @Load 1.12 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 40 % | >= 40 % | 50 mm/min; b.o. ISO 527-1,-2 |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527-1,-2 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-U |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 350 V | 350 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 76.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
42.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75-1,-2 |
| Vicat Softening Point | 95.0 °C @Load 5.10 kg |
203 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 97.0 °C @Load 5.10 kg |
207 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 240 °C | 464 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com