- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.886
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.196
- 拉伸强度 [MPa]: 24.1
- 弯曲强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 0.827
- 硬度: 68.0
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in³ | Average value: 0.903 g/cc Grade Count:89 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:3 |
| Environmental Stress Crack Resistance | >= 500 hour @Temperature 50.0 - 50.0 °C | >= 500 hour @Temperature 122 - 122 °F | Average value: 500 hour Grade Count:2 |
| Linear Mold Shrinkage | 0.0100 - 0.0250 cm/cm | 0.0100 - 0.0250 in/in | Average value: 0.0175 cm/cm Grade Count:4 |
| Melt Flow | 0.300 - 1500 g/10 min | 0.300 - 1500 g/10 min | Average value: 63.5 g/10 min Grade Count:103 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 68.0 - 112 | 68.0 - 112 | Average value: 99.0 Grade Count:44 |
| Hardness, Shore D | 70.0 - 76.0 | 70.0 - 76.0 | Average value: 73.1 Grade Count:16 |
| Tensile Strength, Ultimate | 25.0 - 317 MPa | 3630 - 46000 psi | Average value: 133 MPa Grade Count:19 |
| Tensile Strength, Yield | 24.1 - 40.7 MPa | 3500 - 5900 psi | Average value: 34.9 MPa Grade Count:78 |
| Elongation at Break | 15.0 - 650 % | 15.0 - 650 % | Average value: 268 % Grade Count:19 |
| Elongation at Yield | 6.00 - 203 % | 6.00 - 203 % | Average value: 19.0 % Grade Count:68 |
| Modulus of Elasticity | 1.35 - 1.79 GPa | 196 - 260 ksi | Average value: 1.59 GPa Grade Count:15 |
| Tenacity | 0.168 - 0.353 N/tex | 1.90 - 4.00 g/denier | Average value: 0.255 N/tex Grade Count:14 |
| Flexural Modulus | 0.827 - 1.93 GPa | 120 - 280 ksi | Average value: 1.49 GPa Grade Count:92 |
| Izod Impact, Notched | 0.196 - 0.490 J/cm | 0.367 - 0.919 ft-lb/in | Average value: 0.289 J/cm Grade Count:63 |
| 0.166713 - 0.274586 J/cm @Temperature -20.0 - 0.000 °C | 0.312322 - 0.514412 ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 0.216 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 0.186 J/cm - NB | 0.349 ft-lb/in - NB | Average value: 3.08 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 3.00 - 6.50 kJ/m² | 1.43 - 3.09 ft-lb/in² | Average value: 4.44 kJ/m² Grade Count:8 |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | Average value: 0.450 J/cm² Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 146 - 165 °C | 295 - 329 °F | Average value: 162 °C Grade Count:21 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 - 129 °C | 167 - 264 °F | Average value: 104 °C Grade Count:60 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 104 °C | 126 - 219 °F | Average value: 64.8 °C Grade Count:18 |
| Vicat Softening Point | 78.0 - 155 °C | 172 - 311 °F | Average value: 147 °C Grade Count:35 |
| Heat Distortion Temperature | 95.0 - 119 °C | 203 - 246 °F | Average value: 108 °C Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 - 274 °C | 399 - 525 °F | Average value: 238 °C Grade Count:10 |
| Melt Temperature | 204 - 288 °C | 399 - 550 °F | Average value: 232 °C Grade Count:10 |