- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.886
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 22.8
- 弯曲强度 [MPa]: 23.4
- 弯曲模量 [MPa]: 0.689
- 硬度: 34.0
- 热变形温度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 1.04 g/cc | 0.0320 - 0.0376 lb/in³ | Average value: 0.906 g/cc Grade Count:57 |
| Moisture Vapor Transmission | 7.10 - 9.40 cc-mm/m²-24hr-atm | 18.0 - 23.9 cc-mil/100 in²-24hr-atm | Average value: 9.02 cc-mm/m²-24hr-atm Grade Count:12 |
| Oxygen Transmission | 95.0 cc-mm/m²-24hr-atm | 241 cc-mil/100 in²-24hr-atm | Average value: 95.0 cc-mm/m²-24hr-atm Grade Count:10 |
| Linear Mold Shrinkage | 0.0100 - 0.0250 cm/cm | 0.0100 - 0.0250 in/in | Average value: 0.0173 cm/cm Grade Count:7 |
| Melt Flow | 0.500 - 50.0 g/10 min | 0.500 - 50.0 g/10 min | Average value: 3.27 g/10 min Grade Count:65 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 34.0 - 110 | 34.0 - 110 | Average value: 90.5 Grade Count:32 |
| Hardness, Shore D | 61.0 - 73.0 | 61.0 - 73.0 | Average value: 68.3 Grade Count:4 |
| Tensile Strength, Ultimate | 23.4 - 33.1 MPa | 3390 - 4800 psi | Average value: 28.3 MPa Grade Count:13 |
| Tensile Strength, Yield | 22.8 - 40.3 MPa | 3300 - 5850 psi | Average value: 30.5 MPa Grade Count:51 |
| Elongation at Break | 8.00 - 700 % | 8.00 - 700 % | Average value: 61.3 % Grade Count:18 |
| Elongation at Yield | 4.60 - 20.0 % | 4.60 - 20.0 % | Average value: 11.6 % Grade Count:39 |
| Modulus of Elasticity | 0.827 - 1.38 GPa | 120 - 200 ksi | Average value: 1.08 GPa Grade Count:17 |
| Flexural Modulus | 0.689 - 2.45 GPa | 99.9 - 355 ksi | Average value: 1.20 GPa Grade Count:65 |
| Izod Impact, Notched | 0.200 - 5340 J/cm | 0.375 - 10000 ft-lb/in | Average value: 1.56 J/cm Grade Count:55 |
| 0.170 - 3.41696 J/cm @Temperature -20.0 - 4.00 °C | 0.318 - 6.40137 ft-lb/in @Temperature -4.00 - 39.2 °F | Average value: 1.14 J/cm Grade Count:8 | |
| Izod Impact, Notched (ISO) | 7.50 - 56.0 kJ/m² | 3.57 - 26.6 ft-lb/in² | Average value: 28.5 kJ/m² Grade Count:3 |
| 3.60 - 4.20 kJ/m² @Temperature -40.0 - 0.000 °C | 1.71 - 2.00 ft-lb/in² @Temperature -40.0 - 32.0 °F | Average value: 3.90 kJ/m² Grade Count:2 | |
| Charpy Impact, Notched | 3.00 - 12.0 J/cm² @Temperature -20.0 - 0.000 °C | 14.3 - 57.1 ft-lb/in² @Temperature -4.00 - 32.0 °F | Average value: 7.67 J/cm² Grade Count:2 |
| Gardner Impact | 1.00 - 1.00 J @Temperature -30.0 - -30.0 °C | 0.738 - 0.738 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.00 J Grade Count:1 |
| Tangent Modulus | 869 - 1300 MPa | 126000 - 189000 psi | Average value: 1020 MPa Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 143 - 165 °C | 289 - 329 °F | Average value: 148 °C Grade Count:17 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 - 133 °C | 162 - 271 °F | Average value: 91.7 °C Grade Count:58 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 - 60.0 °C | 113 - 140 °F | Average value: 55.2 °C Grade Count:8 |
| Vicat Softening Point | 67.0 - 156 °C | 153 - 313 °F | Average value: 137 °C Grade Count:11 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.00 - 71.0 % | 8.00 - 71.0 % | Average value: 26.1 % Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 177 - 249 °C | 351 - 480 °F | Average value: 213 °C Grade Count:12 |