- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 24.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Index of Compound | 37 g/10 min @Load 2.16 kg, Temperature 230 °C | 37 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527 |
| Elongation at Break | 500 % | 500 % | ISO R 527 |
| Tensile Modulus | 0.880 GPa | 128 ksi | ISO R 527 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 160 °C | 320 °F | DSC |
| Vicat Softening Point | 138 °C | 280 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 275 °C | 527 °F | |
| Adapter Temperature | 275 °C | 527 °F | |
| Die Temperature | 275 °C | 527 °F | |