Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled

Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled 物性表: Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled物性表及特性介绍,Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled注塑参数详情,如需Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 15.0
  • 密度 [g/cm3]: 1.04
  • 拉伸强度 [MPa]: 31.0
  • 热变形温度 [℃]: 114.0
 
Physical PropertiesMetricEnglishComments
Density 1.04 g/cc0.0376 lb/in³
Melt Flow 15 g/10 min
@Load 2.16 kg,
Temperature 230 °C
15 g/10 min
@Load 4.76 lb,
Temperature 446 °F
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 31.0 MPa4500 psi50 mm/min
Elongation at Break 15 %15 %Nominal Strain; 50 mm/min
Elongation at Yield 4.5 %4.5 %50 mm/min
Tensile Modulus 2.17 GPa315 ksi1 mm/min
Charpy Impact, Notched 0.520 J/cm²2.47 ft-lb/in²
 0.300 J/cm²
@Temperature -30.0 °C
1.43 ft-lb/in²
@Temperature -22.0 °F
 
Thermal PropertiesMetricEnglishComments
Melting Point 163 °C325 °F10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 114 °C237 °F
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C136 °F
Vicat Softening Point 93.0 °C199 °F50°C/hr; 50N

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31051.html

免责声明: 本文 Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4