- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 24.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Index of Compound | 3.8 g/10 min @Load 2.16 kg, Temperature 210 °C | 3.8 g/10 min @Load 4.76 lb, Temperature 410 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ISO 608 |
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D527-2 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527-2 |
| Elongation at Break | 540 % | 540 % | ISO R 527-2 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 152 °C | 306 °F | DSC |
| Vicat Softening Point | 126 °C @Load 0.999 kg | 259 °F @Load 2.20 lb | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 190 - 210 °C | 374 - 410 °F | |
| Zone 2 | 195 - 220 °C | 383 - 428 °F | |
| Zone 3 | 200 - 225 °C | 392 - 437 °F | |
| Zone 4 | 205 - 230 °C | 401 - 446 °F | |
| Die Temperature | 220 - 240 °C | 428 - 464 °F | |