- 熔体流动速率 [g/10min]: 3.0
- 缺口冲击强度: 0.53
- 弯曲模量 [MPa]: 2.892
- 热变形温度 [℃]: 112.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 | ||
| Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 | ||
| Elongation at Break | 23 % | 23 % | ASTM D638 | ||
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 | ||
| Flexural Modulus | 2.892 GPa | 419.5 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 5.29 J/cm | 9.91 ft-lb/in | ASTM D4812 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 | ||
| DSC Induction Temperature | 165 °C | 329 °F | at 10aC/min; ASTM D3418 | ||
| Descriptive Properties | |||||
| Flammability | SE | FMVSS 302 | |||
| Surface Resistivity | 89 | R-Scale (ASTM D785) | |||