- 熔体流动速率 [g/10min]: 0.9
- 缺口冲击强度: 3.2
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.45
- 硬度: 90.0
- 热变形温度 [℃]: 113.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 | ||
| Melt Flow | 0.90 g/10 min @Temperature 230 °C | 0.90 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 90 | 90 | ASTM D785 | ||
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 | ||
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 | ||
| Elongation at Yield | 30 % | 30 % | ASTM D638 | ||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 | ||
| Izod Impact, Notched | 3.20 J/cm | 6.00 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | NB | NB | -22°F; ASTM D256 | ||
| Gardner Impact | 14.47 J | 10.67 ft-lb | ASTM D3029 | ||
| 43.4 J @Temperature -28.9 °C | 32.0 ft-lb @Temperature -20.0 °F | ASTM D3029 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
| 62.8 °C | 145 °F | ASTM D648 | |||
| Descriptive Properties | |||||
| Thermal Oxidative Stability | Pass | ASTM D3012, at 336 hrs, 150°C | |||