- 熔体流动速率 [g/10min]: 5.0
- 缺口冲击强度: 0.64
- 拉伸强度 [MPa]: 25.5
- 弯曲模量 [MPa]: 1.725
- 硬度: 87.0
- 热变形温度 [℃]: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | ASTM D638 |
| Flexural Modulus | 1.725 GPa | 250.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |