- 缺口冲击强度: 1.92
- 拉伸强度 [MPa]: 20.7
- 弯曲模量 [MPa]: 0.931
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc @Temperature 23.0 °C | 0.900 g/cc @Temperature 73.4 °F | ASTM D792 |
| Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C | 35 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Modulus | 0.931 GPa | 135 ksi | 0.05 in/min, 1% Secant; ASTM D790 |
| Izod Impact, Notched | 1.92 J/cm @Temperature 22.8 °C | 3.60 ft-lb/in @Temperature 73.0 °F | Method A; ASTM D256 |