- 密度 [g/cm3]: 0.901
- 缺口冲击强度: 1.23
- 拉伸强度 [MPa]: 24.5
- 弯曲模量 [MPa]: 1.10
- 硬度: 104.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.901 g/cc | 0.0326 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 22 g/10 min @Temperature 230 °C | 22 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 24.5 MPa | 3550 psi | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 1% Secant; ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Temperature 22.8 °C | 2.30 ft-lb/in @Temperature 73.0 °F | ASTM D256 |