- 密度 [g/cm3]: 0.903
- 缺口冲击强度: 0.374
- 拉伸强度 [MPa]: 39.3
- 弯曲模量 [MPa]: 1.52
- 硬度: 109.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.903 g/cc | 0.0326 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 4.0 g/10 min @Temperature 230 °C | 4.0 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 39.3 MPa | 5700 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | 1.3 mm/min, 1% Secant; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C | 0.700 ft-lb/in @Temperature 73.0 °F | ASTM D256 |