- 密度 [g/cm3]: 1.7
- 弯曲强度 [MPa]: 69.0
- 弯曲模量 [MPa]: 13.0
- 热变形温度 [℃]: 260.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
Water Absorption | <= 0.10 % | <= 0.10 % | ISO 62 |
Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ISO 527-1 |
Elongation at Break | 0.60 % | 0.60 % | ISO 527-1 |
Tensile Modulus | 25.0 GPa | 3630 ksi | ISO 527-1 |
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
Charpy Impact Unnotched | 0.370 J/cm² | 1.76 ft-lb/in² | ISO 179-1 |
Charpy Impact, Notched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
Surface Resistivity per Square | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
Thermal Properties | Metric | English | Comments |
Specific Heat Capacity | 1.00 J/g-°C | 0.239 BTU/lb-°F | ASTM E1461 |
Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | ASTM E1461 |
Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75-1/-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 |
Flammability, UL94 | V-0 @Thickness 1.00 mm | V-0 @Thickness 0.0394 in | |
Processing Properties | Metric | English | Comments |
Rear Barrel Temperature | 330 - 360 °C | 626 - 680 °F | |
Middle Barrel Temperature | 340 - 370 °C | 644 - 698 °F | |
Front Barrel Temperature | 345 - 380 °C | 653 - 716 °F | |
Nozzle Temperature | 350 - 382 °C | 662 - 720 °F | |
Melt Temperature | 349 - 393 °C | 660 - 739 °F | |
Mold Temperature | 93.0 - 177 °C | 199 - 351 °F | |
Drying Temperature | 180 °C | 356 °F | |
Dry Time | 2 - 4 hour | 2 - 4 hour | |
Moisture Content | 0.010 % | 0.010 % | |
Dew Point | -34.0 °C | -29.2 °F | |
Injection Pressure | 35.0 - 70.0 MPa | 5080 - 10200 psi | |
Hold Pressure | 7.00 - 35.0 MPa | 1020 - 5080 psi | |
Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |
Screw Speed | 75 - 150 rpm | 75 - 150 rpm |