- 密度 [g/cm3]: 1.77
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 14.5
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.77 g/cc | 0.0639 lb/in³ | ISO 1183 | ||
Filler Content | 40 % | 40 % | |||
Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Thickness 2.00 mm | 0.00050 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | ISO 294-4 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 | ||
Elongation at Break | 1.3 % | 1.3 % | ISO 527 | ||
Tensile Modulus | 17.3 GPa @Temperature 23.0 °C | 2510 ksi @Temperature 73.4 °F | ISO 527 | ||
Flexural Strength | 200 MPa @Temperature 23.0 °C | 29000 psi @Temperature 73.4 °F | ISO 178 | ||
Flexural Modulus | 14.5 GPa @Temperature 23.0 °C | 2100 ksi @Temperature 73.4 °F | ISO 178 | ||
Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | ||
20.0 kJ/m² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
Charpy Impact Unnotched | 1.80 J/cm² @Temperature -30.0 °C | 8.57 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Comparative Tracking Index | 175 - 249 V | 175 - 249 V | UL 746A | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 0.000 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | 0.000 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | ||
2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | 1.11 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 260 °C | 1.67 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 260 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 500 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
3.00 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 1.67 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
4.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 2.22 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
5.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 2.78 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 30.6 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 2mm | ||
56.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 31.1 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 4mm | |||
77.0 µm/m-°C @Temperature -40.0 - 260 °C | 42.8 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 2mm | |||
79.0 µm/m-°C @Temperature -40.0 - 260 °C | 43.9 µin/in-°F @Temperature -40.0 - 500 °F | ISO 11359-1/-2; 4mm | |||
62.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 34.4 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
64.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 35.6 µin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
80.0 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C | 44.4 µin/in-°F @Thickness 0.0787 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
82.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 45.6 µin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
90.0 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C | 50.0 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
94.0 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C | 52.2 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F | ISO 11359-1/-2 | |||
Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1/-3 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 | ||
UL RTI, Electrical | 240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | ||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical with Impact | 220 °C @Thickness 1.50 mm | 428 °F @Thickness 0.0591 in | UL 746B | ||
220 °C @Thickness 3.00 mm | 428 °F @Thickness 0.118 in | UL 746B | |||
UL RTI, Mechanical without Impact | 240 °C @Thickness 1.50 mm | 464 °F @Thickness 0.0591 in | UL 746B | ||
240 °C @Thickness 3.00 mm | 464 °F @Thickness 0.118 in | UL 746B | |||
Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | ||
V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 355 °C | 671 °F | Optimum | ||
350 - 360 °C | 662 - 680 °F | ||||
Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
40.0 - 150 °C | 104 - 302 °F | ||||
Drying Temperature | 150 °C | 302 °F | |||
Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
Moisture Content | <= 0.010 % | <= 0.010 % | |||
Descriptive Properties | |||||
Color | White | ||||
Drying Recommended | Yes | ||||
Filler | Glass Reinforced | ||||
Flame Retardant - Halogen/Red Phosphorus Free | Yes | ||||
Forms | Pellets | ||||
Generic | LCP | ||||
Part Marking Code | >LCP-GF40< | ISO 11469 | |||
Polymer Family | LCP | ||||
Polymer Type | LCP | ||||
Processing | Injection Moldable | ||||
Processing Method | Injection Molding | ||||
Product Category | Electrical Resins | ||||
Electrical Resins | |||||
Flame Retardant Resins | |||||
Flame Retardant Resins | |||||
Glass Reinforced Resins | |||||
Glass Reinforced Resins | |||||
Region Available | Americas | ||||
Asia/Pacific | |||||
Europe | |||||
Resin Identification | LCP-GF40 | ISO 1043 |