- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.247
- 缺口冲击强度: 0.153
- 断裂伸长率 [%]: 68.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 - 1.43 g/cc | 0.0491 - 0.0517 lb/in³ | Average value: 1.40 g/cc Grade Count:31 |
| Apparent Bulk Density | 0.560 - 0.620 g/cc | 0.0202 - 0.0224 lb/in³ | Average value: 0.593 g/cc Grade Count:6 |
| Water Absorption | 0.247 - 0.640 % | 0.247 - 0.640 % | Average value: 0.387 % Grade Count:31 |
| Linear Mold Shrinkage | 0.00340 - 0.0109 cm/cm | 0.00340 - 0.0109 in/in | Average value: 0.00668 cm/cm Grade Count:31 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 75.0 - 93.0 | 75.0 - 93.0 | Average value: 86.8 Grade Count:25 |
| Tensile Strength, Ultimate | 45.0 - 64.0 MPa | 6530 - 9280 psi | Average value: 54.5 MPa Grade Count:31 |
| Elongation at Break | 0.410 - 0.920 % | 0.410 - 0.920 % | Average value: 0.738 % Grade Count:25 |
| Modulus of Elasticity | 7.60 - 9.40 GPa | 1100 - 1360 ksi | Average value: 8.40 GPa Grade Count:25 |
| Flexural Yield Strength | 68.0 - 97.0 MPa | 9860 - 14100 psi | Average value: 83.4 MPa Grade Count:31 |
| Flexural Modulus | 6.80 - 9.00 GPa | 986 - 1310 ksi | Average value: 7.82 GPa Grade Count:31 |
| Compressive Yield Strength | 155 - 234 MPa | 22500 - 33900 psi | Average value: 208 MPa Grade Count:31 |
| Poissons Ratio | 0.330 - 0.360 | 0.330 - 0.360 | Average value: 0.352 Grade Count:11 |
| Shear Modulus | 2.79 - 3.22 GPa | 405 - 467 ksi | Average value: 3.00 GPa Grade Count:11 |
| Izod Impact, Notched | 0.153 - 0.241 J/cm | 0.287 - 0.451 ft-lb/in | Average value: 0.187 J/cm Grade Count:25 |
| Charpy Impact, Notched | 0.178 - 0.249 J/cm² | 0.847 - 1.19 ft-lb/in² | Average value: 0.196 J/cm² Grade Count:25 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.60e+11 - 5.00e+13 ohm-cm | 1.60e+11 - 5.00e+13 ohm-cm | Average value: 2.81e+12 ohm-cm Grade Count:30 |
| Dielectric Constant | 4.00 - 6.10 | 4.00 - 6.10 | Average value: 5.09 Grade Count:30 |
| Dielectric Strength | 8.50 - 16.7 kV/mm | 216 - 424 kV/in | Average value: 12.0 kV/mm Grade Count:30 |
| Dissipation Factor | 0.0300 - 0.100 | 0.0300 - 0.100 | Average value: 0.0531 Grade Count:30 |
| Arc Resistance | 25.0 - 144 sec | 25.0 - 144 sec | Average value: 119 sec Grade Count:24 |
| Comparative Tracking Index | 125 - 200 V | 125 - 200 V | Average value: 160 V Grade Count:30 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 43.0 - 99.0 µm/m-°C @Temperature 40.0 - 130 °C | 23.9 - 55.0 µin/in-°F @Temperature 104 - 266 °F | Average value: 62.3 µm/m-°C Grade Count:22 |
| Thermal Conductivity | 0.340 - 0.440 W/m-K @Temperature 100 - 100 °C | 2.36 - 3.05 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 0.384 W/m-K Grade Count:15 |
| Maximum Service Temperature, Air | 187 - 207 °C | 369 - 405 °F | Average value: 198 °C Grade Count:25 |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 - 186 °C | 288 - 367 °F | Average value: 168 °C Grade Count:31 |
| UL RTI, Electrical | 150 °C | 302 °F | Average value: 150 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:6 |
| Flammability, UL94 | HB - V-1 | HB - V-1 | Grade Count:29 |
| Oxygen Index | 24.5 - 29.1 % | 24.5 - 29.1 % | Average value: 26.4 % Grade Count:23 |
| Shrinkage | 0.143 - 0.460 % | 0.143 - 0.460 % | Average value: 0.270 % Grade Count:25 |