- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 0.155
- 缺口冲击强度: 0.233
- 断裂伸长率 [%]: 56.0
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 3.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 - 1.60 g/cc | 0.0484 - 0.0578 lb/in³ | Average value: 1.51 g/cc Grade Count:3 |
| Water Absorption | 0.155 - 0.920 % | 0.155 - 0.920 % | Average value: 0.413 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00110 - 0.00790 cm/cm | 0.00110 - 0.00790 in/in | Average value: 0.00378 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 43.0 - 76.0 | 43.0 - 76.0 | Average value: 54.3 Grade Count:3 |
| Tensile Strength, Ultimate | 34.0 - 74.0 MPa | 4930 - 10700 psi | Average value: 54.7 MPa Grade Count:3 |
| Elongation at Break | 0.730 - 1.47 % | 0.730 - 1.47 % | Average value: 0.983 % Grade Count:3 |
| Modulus of Elasticity | 4.50 - 9.60 GPa | 653 - 1390 ksi | Average value: 7.77 GPa Grade Count:3 |
| Flexural Yield Strength | 56.0 - 115 MPa | 8120 - 16700 psi | Average value: 87.0 MPa Grade Count:3 |
| Flexural Modulus | 3.60 - 8.90 GPa | 522 - 1290 ksi | Average value: 6.97 GPa Grade Count:3 |
| Compressive Yield Strength | 82.0 - 157 MPa | 11900 - 22800 psi | Average value: 118 MPa Grade Count:3 |
| Izod Impact, Notched | 0.233 - 0.470 J/cm | 0.437 - 0.881 ft-lb/in | Average value: 0.364 J/cm Grade Count:3 |
| Charpy Impact, Notched | 0.281 - 0.450 J/cm² | 1.34 - 2.14 ft-lb/in² | Average value: 0.357 J/cm² Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+11 - 6.40e+11 ohm-cm | 2.00e+11 - 6.40e+11 ohm-cm | Average value: 4.87e+11 ohm-cm Grade Count:3 |
| Dielectric Constant | 4.50 - 5.80 | 4.50 - 5.80 | Average value: 5.27 Grade Count:3 |
| Dielectric Strength | 10.5 - 13.2 kV/mm | 267 - 335 kV/in | Average value: 12.0 kV/mm Grade Count:3 |
| Dissipation Factor | 0.0770 - 0.0830 | 0.0770 - 0.0830 | Average value: 0.0803 Grade Count:3 |
| Arc Resistance | 67.0 - 135 sec | 67.0 - 135 sec | Average value: 107 sec Grade Count:3 |
| Comparative Tracking Index | 150 - 175 V | 150 - 175 V | Average value: 167 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 53.0 - 53.0 µm/m-°C @Temperature 40.0 - 130 °C | 29.4 - 29.4 µin/in-°F @Temperature 104 - 266 °F | Average value: 53.0 µm/m-°C Grade Count:1 |
| Thermal Conductivity | 0.440 - 0.440 W/m-K @Temperature 100 - 100 °C | 3.05 - 3.05 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 0.440 W/m-K Grade Count:1 |
| Maximum Service Temperature, Air | 92.0 - 244 °C | 198 - 471 °F | Average value: 148 °C Grade Count:8 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 - 241 °C | 277 - 466 °F | Average value: 203 °C Grade Count:3 |
| Oxygen Index | 24.6 - 37.0 % | 24.6 - 37.0 % | Average value: 32.5 % Grade Count:3 |
| Shrinkage | 0.0700 - 0.390 % | 0.0700 - 0.390 % | Average value: 0.196 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | Average value: 166 °C Grade Count:5 |
| Cure Time | 0.583 - 3.00 min | 0.00972 - 0.0500 hour | Average value: 1.63 min Grade Count:5 |