- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.18
- 缺口冲击强度: 0.21
- 断裂伸长率 [%]: 61.0
- 弯曲强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 - 1.45 g/cc | 0.0499 - 0.0524 lb/in³ | Average value: 1.41 g/cc Grade Count:7 |
| Water Absorption | 0.180 - 0.630 % | 0.180 - 0.630 % | Average value: 0.436 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00300 - 0.00850 cm/cm | 0.00300 - 0.00850 in/in | Average value: 0.00576 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 63.0 - 91.0 | 63.0 - 91.0 | Average value: 77.7 Grade Count:7 |
| Tensile Strength, Ultimate | 36.0 - 55.7 MPa | 5220 - 8080 psi | Average value: 48.6 MPa Grade Count:7 |
| Elongation at Break | 0.710 - 1.00 % | 0.710 - 1.00 % | Average value: 0.817 % Grade Count:6 |
| Modulus of Elasticity | 6.90 - 8.27 GPa | 1000 - 1200 ksi | Average value: 7.70 GPa Grade Count:6 |
| Flexural Yield Strength | 61.0 - 83.2 MPa | 8850 - 12100 psi | Average value: 74.2 MPa Grade Count:7 |
| Flexural Modulus | 6.20 - 7.72 GPa | 899 - 1120 ksi | Average value: 7.12 GPa Grade Count:7 |
| Compressive Yield Strength | 139 - 213 MPa | 20200 - 30900 psi | Average value: 175 MPa Grade Count:7 |
| Poissons Ratio | 0.300 - 0.350 | 0.300 - 0.350 | Average value: 0.338 Grade Count:4 |
| Shear Modulus | 2.56 - 3.00 GPa | 371 - 435 ksi | Average value: 2.87 GPa Grade Count:4 |
| Izod Impact, Notched | 0.210 - 0.277 J/cm | 0.393 - 0.519 ft-lb/in | Average value: 0.241 J/cm Grade Count:6 |
| Charpy Impact, Notched | 0.199 - 0.400 J/cm² | 0.947 - 1.90 ft-lb/in² | Average value: 0.271 J/cm² Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.38e+10 - 2.13e+12 ohm-cm | 6.38e+10 - 2.13e+12 ohm-cm | Average value: 5.65e+11 ohm-cm Grade Count:7 |
| Dielectric Constant | 4.50 - 6.60 | 4.50 - 6.60 | Average value: 5.14 Grade Count:7 |
| Dielectric Strength | 7.90 - 16.2 kV/mm | 201 - 411 kV/in | Average value: 11.1 kV/mm Grade Count:7 |
| Dissipation Factor | 0.0400 - 0.0760 | 0.0400 - 0.0760 | Average value: 0.0560 Grade Count:7 |
| Arc Resistance | 26.0 - 160 sec | 26.0 - 160 sec | Average value: 110 sec Grade Count:7 |
| Comparative Tracking Index | 150 - 175 V | 150 - 175 V | Average value: 168 V Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 44.0 - 67.0 µm/m-°C @Temperature 40.0 - 130 °C | 24.4 - 37.2 µin/in-°F @Temperature 104 - 266 °F | Average value: 54.0 µm/m-°C Grade Count:3 |
| Thermal Conductivity | 0.370 - 0.400 W/m-K @Temperature 100 - 100 °C | 2.57 - 2.78 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 0.385 W/m-K Grade Count:2 |
| Maximum Service Temperature, Air | 170 - 200 °C | 338 - 392 °F | Average value: 189 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 - 196 °C | 313 - 385 °F | Average value: 173 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:7 |
| Oxygen Index | 24.2 - 27.1 % | 24.2 - 27.1 % | Average value: 25.7 % Grade Count:3 |
| Shrinkage | 0.220 - 0.430 % | 0.220 - 0.430 % | Average value: 0.325 % Grade Count:4 |