- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.32
- 弯曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ASTM D1895 | ||
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | ASTM D570 | ||
| 0.50 % @Time 173000 sec | 0.50 % @Time 48.0 hour | ASTM D570 | |||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 | ||
| Flexural Strength | 62.0 MPa | 8990 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 | ||
| Compressive Strength | 172 MPa | 24900 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.8 @Frequency 1.00e+6 Hz | 4.8 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 11.0 kV/mm @Frequency 60.0 Hz | 279 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 13.7 kV/mm @Frequency 60.0 Hz | 348 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | As Molded; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellet | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||