- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.6
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.400 g/cc | 0.0145 lb/in³ | Powder; ASTM D1895 | ||
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D-792 | ||
| Water Absorption | 0.60 % | 0.60 % | 24 hour; ASTM D570 | ||
| 1.5 % | 1.5 % | 48 hour; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 70 | 70 | ASTM D785 | ||
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 | ||
| Flexural Strength | 70.0 MPa | 10200 psi | ASTM D790 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 | ||
| Compressive Strength | 200 MPa | 29000 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 3.40 kV/mm | 86.4 kV/in | 60 Hz, wet, SS; ASTM D149 | ||
| 5.90 kV/mm | 150 kV/in | ST; ASTM D149 | |||
| Arc Resistance | 65 sec | 65 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature 20.0 °C | 26.1 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature 20.0 °C | 29.4 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Thermal Conductivity | 0.560 W/m-K | 3.89 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | As Molded; ASTM D648A | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black | ||||
| Form | Pellet | ||||