- 密度 [g/cm3]: 1.75
- 缺口冲击强度: 2.67
- 断裂伸长率 [%]: 137
- 弯曲强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM D638 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ASTM D638 |
| Flexural Yield Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 | V-0 | 5V UL94 at 1 mm |
| Oxygen Index | 46 % | 46 % | ASTM D2863 |
| Shrinkage | 0.0010 % | 0.0010 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 160 °C | 270 - 320 °F | Mold temperature |