Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste

Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste 物性表: Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste物性表及特性介绍,Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste注塑参数详情,如需Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.41
  • 弯曲模量 [MPa]: 7.00
 
Physical PropertiesMetricEnglishComments
Density 1.41 g/cc0.0509 lb/in³ISO 1183
Apparent Bulk Density 0.620 g/cc0.0224 lb/in³ISO 60
Linear Mold Shrinkage, Flow 0.0065 cm/cm0.0065 in/inCompression molding; ISO 2577
 
Mechanical PropertiesMetricEnglishComments
Flexural Strength 90.0 MPa13100 psi2 mm/min; ISO 178
Flexural Modulus 7.00 GPa1020 ksiISO 178
Charpy Impact Unnotched 0.550 J/cm²
@Temperature 23.0 °C
2.62 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eU
Charpy Impact, Notched 0.130 J/cm²
@Temperature 23.0 °C
0.619 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+11 ohm-cm1.00e+11 ohm-cmIEC 60093
Surface Resistance 1.00e+10 ohm1.00e+10 ohmIEC 60093
Dielectric Constant 15
@Frequency 100 Hz
15
@Frequency 100 Hz
IEC 60250
Dielectric Strength 15.0 kV/mm
@Thickness 1.00 mm
381 kV/in
@Thickness 0.0394 in
IEC 60243-P1
Dissipation Factor 0.40
@Frequency 100 Hz
0.40
@Frequency 100 Hz
IEC 60250
Arc Resistance 60 - 120 sec
@Thickness 3.00 mm
60 - 120 sec
@Thickness 0.118 in
(BK)
High Voltage Arc Resistance to Ignition (HVAR) >= 300 sec
@Thickness 1.50 mm
>= 300 sec
@Thickness 0.0591 in
BK
Comparative Tracking Index 100 - 175 V
@Thickness 3.00 mm
100 - 175 V
@Thickness 0.118 in
(BK)
Hot Wire Ignition, HWI >= 120 sec
@Thickness 1.50 mm
>= 120 sec
@Thickness 0.0591 in
BK
High Amp Arc Ignition, HAI  30 - 60 arcs
@Thickness 1.50 mm
30 - 60 arcs
@Thickness 0.0591 in
BK
 60 - 120 arcs
@Thickness 3.00 mm
60 - 120 arcs
@Thickness 0.118 in
(BK)
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
@Thickness 1.50 mm
0.000 - 0.394 in/min
@Thickness 0.0591 in
BK
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 8.0 MPa 105 °C221 °FISO 75-2
UL RTI, Electrical 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
BK
UL RTI, Mechanical with Impact 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
BK
UL RTI, Mechanical without Impact 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
BK
Flammability, UL94  V-1
@Thickness 1.50 mm
V-1
@Thickness 0.0591 in
BK
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
(BK)
Shrinkage 0.65 %0.65 %Compression molding, 168 hours/110°C; ISO 2577
 
Processing PropertiesMetricEnglishComments
Feed Temperature 60.0 - 75.0 °C140 - 167 °FInjection molding
Nozzle Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Melt Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Mold Temperature 160 - 190 °C320 - 374 °FInjection molding
 160 - 190 °C320 - 374 °FCompression molding
Injection Pressure >= 15.0 MPa>= 2180 psiCompression and injection cavity mold pressure
Back Pressure 0.500 - 2.00 MPa72.5 - 290 psiInjection molding
Cure Time 0.167 - 0.333 min0.00278 - 0.00556 hourPer 1 mm of wall thickness, injection molding
 0.333 - 0.667 min0.00556 - 0.0111 hourPer 1 mm of wall thickness, compression molding
 
Descriptive Properties
Chromatic SpectrumSubdued Colors
Creep Rupture StrengthGood
Holding PressureApproximately 40-60% of injection pressure
Media ResistanceGood
Moisture Absorption80 mgISO 62, 24 hours at 23°C
Reserves by Peak TemperatureHigh
Thermal ExpansionSlight

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34896.html

免责声明: 本文 Momentive Performance Materials PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Liste 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4