- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.181
- 缺口冲击强度: 0.205
- 弯曲强度 [MPa]: 46.0
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.181 % | 0.181 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 0.52 % | 0.52 % | ASTM D638 |
| Tensile Modulus | 10.2 GPa | 1480 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
| Compressive Strength | 159 MPa | 23100 psi | ASTM D695 |
| Izod Impact, Notched | 0.205 J/cm | 0.384 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.212 J/cm² | 1.01 ft-lb/in² | ASTM D256 |
| Impact | 89 | 89 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.50e+11 ohm-cm | 4.50e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 7.70 kV/mm | 196 kV/in | Step by Step; ASTM D149 |
| 11.5 kV/mm | 292 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.062 | 0.062 | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 56.0 µm/m-°C @Temperature 40.0 - 130 °C | 31.1 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 208 °C | 406 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Shrinkage | 0.147 % | 0.147 % | 72 hr, 120ºC; ASTM D1299 |