- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.45
- 缺口冲击强度: 0.199
- 弯曲强度 [MPa]: 59.0
- 弯曲模量 [MPa]: 8.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Water Absorption | 0.45 % | 0.45 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Compressive Strength | 217 MPa | 31500 psi | ASTM D695 |
| Izod Impact, Notched | 0.199 J/cm | 0.373 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.193 J/cm² | 0.919 ft-lb/in² | ASTM D256 |
| Impact | 130 | 130 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.00e+12 ohm-cm | 6.00e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.6 | 4.6 | ASTM D150 |
| Dielectric Strength | 14.3 kV/mm | 363 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.038 | 0.038 | ASTM D150 |
| Arc Resistance | 103 sec | 103 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 68.0 µm/m-°C @Temperature 40.0 - 130 °C | 37.8 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.370 W/m-K @Temperature 100 °C | 2.57 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 196 °C | 385 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Shrinkage | 0.195 % | 0.195 % | 72 hr, 120ºC; ASTM D1299 |