- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.212
- 缺口冲击强度: 0.151
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D1895 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.212 % | 0.212 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0081 cm/cm | 0.0081 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 0.82 % | 0.82 % | ASTM D638 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | ASTM D638 |
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Compressive Strength | 195 MPa | 28300 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.00 GPa | 435 ksi | Calculated |
| Izod Impact, Notched | 0.151 J/cm | 0.283 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.172 J/cm² | 0.819 ft-lb/in² | ASTM D256 |
| Impact | 96 | 96 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.90e+11 ohm-cm | 1.90e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.3 | 5.3 | ASTM D150 |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.056 | 0.056 | ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.8 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 203 °C | 397 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.00 mm | V-1 @Thickness 0.118 in | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |
| Shrinkage | 0.29 % | 0.29 % | 72 hr, 120ºC; ASTM D1299 |