- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.36
- 缺口冲击强度: 0.156
- 弯曲强度 [MPa]: 58.0
- 弯曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.680 g/cc | 0.0246 lb/in³ | ASTM D1895 |
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Water Absorption | 0.36 % | 0.36 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 83 | 83 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 0.91 % | 0.91 % | ASTM D638 |
| Tensile Modulus | 8.90 GPa | 1290 ksi | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Strength | 200 MPa | 29000 psi | ASTM D695 |
| Izod Impact, Notched | 0.156 J/cm | 0.292 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.196 J/cm² | 0.933 ft-lb/in² | ASTM D256 |
| Impact | 102 | 102 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.20e+13 ohm-cm | 4.20e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.7 | 5.7 | ASTM D150 |
| Dielectric Strength | 11.6 kV/mm | 295 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.033 | 0.033 | ASTM D150 |
| Arc Resistance | 86 sec | 86 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 53.0 µm/m-°C @Temperature 40.0 - 130 °C | 29.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Shrinkage | 0.284 % | 0.284 % | 72 hr, 120ºC; ASTM D1299 |