- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.118
- 缺口冲击强度: 0.155
- 弯曲强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D1895 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.118 % | 0.118 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 0.71 % | 0.71 % | ASTM D638 |
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| Compressive Strength | 197 MPa | 28600 psi | ASTM D695 |
| Izod Impact, Notched | 0.155 J/cm | 0.290 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.188 J/cm² | 0.895 ft-lb/in² | ASTM D256 |
| Impact | 97 | 97 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.90e+11 ohm-cm | 1.90e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.8 | 5.8 | ASTM D150 |
| Dielectric Strength | 11.1 kV/mm | 282 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.063 | 0.063 | ASTM D150 |
| Arc Resistance | 170 sec | 170 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.0 µm/m-°C @Temperature 40.0 - 130 °C | 21.1 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 213 °C | 415 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Shrinkage | 0.173 % | 0.173 % | 72 hr, 120ºC; ASTM D1299 |