- 密度 [g/cm3]: 1.81
- 吸水率 [%]: 0.044
- 缺口冲击强度: 0.156
- 弯曲强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.870 g/cc | 0.0314 lb/in³ | ASTM D1895 |
| Density | 1.81 g/cc | 0.0654 lb/in³ | ASTM D792 |
| Water Absorption | 0.044 % | 0.044 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00185 cm/cm | 0.00185 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 59 | 59 | ASTM D785 |
| Tensile Strength, Ultimate | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 0.40 % | 0.40 % | ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Compressive Strength | 134 MPa | 19400 psi | ASTM D695 |
| Izod Impact, Notched | 0.156 J/cm | 0.292 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.176 J/cm² | 0.838 ft-lb/in² | ASTM D256 |
| Impact | 57 | 57 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 µm/m-°C @Temperature 40.0 - 130 °C | 17.8 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 1.22 W/m-K @Temperature 100 °C | 8.47 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 211 °C | 412 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |
| Shrinkage | 0.057 % | 0.057 % | 72 hr, 120ºC; ASTM D1299 |