- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.071
- 缺口冲击强度: 0.43
- 弯曲强度 [MPa]: 93.0
- 弯曲模量 [MPa]: 14.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D792 |
| Water Absorption | 0.071 % | 0.071 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0022 cm/cm | 0.0022 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 97 | 97 | ASTM D785 |
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 0.73 % | 0.73 % | ASTM D638 |
| Tensile Modulus | 15.9 GPa | 2310 ksi | ASTM D638 |
| Flexural Strength | 177 MPa | 25700 psi | ASTM D790 |
| Flexural Modulus | 14.8 GPa | 2150 ksi | ASTM D790 |
| Compressive Strength | 251 MPa | 36400 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 5.98 GPa | 867 ksi | Calculated |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.390 J/cm² | 1.86 ft-lb/in² | ASTM D256 |
| Impact | 310 | 310 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.10e+12 ohm-cm | 1.10e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.6 | 4.6 | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.286 | 0.286 | ASTM D150 |
| Arc Resistance | 70 sec | 70 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 226 °C | 439 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Shrinkage | 0.050 % | 0.050 % | 72 hr, 120ºC; ASTM D1299 |